Highly workable, high strength cement compositions
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C04B-007/26
C04B-024/00
C04B-024/04
C04B-024/06
C04B-024/34
C04B-024/38
C04B-028/02
C04B-007/24
출원번호
US-0070192
(2013-11-01)
등록번호
US-9394200
(2016-07-19)
발명자
/ 주소
Diaz-Loya, Ivan
Patel, Rajeshkumar
Hoffman, David
Trzpekowski, Joseph
Kinney, Frederick
출원인 / 주소
Ceratech Inc
대리인 / 주소
Morrison & Foerster LLP
인용정보
피인용 횟수 :
0인용 특허 :
15
초록▼
Pozzolanic cement compositions and method manufacturing the same are described. These cement compositions may include a pozzolanic material and an activator based on a salt of glycolic acid, glyceric acid, malic acid, tartaric acid, malonic acid, glutaric acid, maleic acid, formic acid, acetic acid,
Pozzolanic cement compositions and method manufacturing the same are described. These cement compositions may include a pozzolanic material and an activator based on a salt of glycolic acid, glyceric acid, malic acid, tartaric acid, malonic acid, glutaric acid, maleic acid, formic acid, acetic acid, propionic acid, or butyric acid, a retarder based on hepto-gluconates, sulfate salts, sugars, sugar acids, lignins, and/or an accelerator based on amines. The cement compositions may have less than 10% by weight Portland cement. The pozzolanic cement compositions including these activators, accelerators, and retarders can have improved properties such as longer setting time, better slump retention, and improved strength.
대표청구항▼
1. A pozzolanic cement composition comprising: a pozzolanic material, andan activator comprising a salt of glycolic acid, glyceric acid, malic acid, tartaric acid, malonic acid, glutaric acid, maleic acid, formic acid, acetic acid, propionic acid, or butyric acid present in an amount of 0.1 to 30% o
1. A pozzolanic cement composition comprising: a pozzolanic material, andan activator comprising a salt of glycolic acid, glyceric acid, malic acid, tartaric acid, malonic acid, glutaric acid, maleic acid, formic acid, acetic acid, propionic acid, or butyric acid present in an amount of 0.1 to 30% of the total weight of the pozzolanic cement composition, wherein the pozzolanic cement composition has less than 10% by weight Portland cement. 2. The pozzolanic cement composition of claim 1, wherein the total amount of the salt of glycolic acid, glyceric acid, malic acid, tartaric acid, malonic acid, glutaric acid, maleic acid, formic acid, acetic acid, propionic acid, and butyric acid comprises more than 95% by weight of the total weight of activators in the pozzolanic cement composition. 3. The pozzolanic cement composition of claim 1 further comprising a retarder selected from the group consisting of sulfate salts, sugars, sugar acids, lignins, boron compounds or combinations thereof. 4. The pozzolanic cement composition of claim 1, wherein the pozzolanic cement composition is substantially free of Portland cement. 5. The pozzolanic cement composition of claim 1, wherein the pozzolanic cement composition has a set time of between 0.5 hours and 24 hours. 6. The pozzolanic cement composition of claim 1, wherein the pozzolanic material is selected from the group consisting of Class C fly-ash, Class F fly-ash, Class N pozzolanic ash, and combinations thereof. 7. The pozzolanic cement composition of claim 1, wherein the pozzolanic cement composition has a silica to calcia molar ratio of between about 1.2:1 and 1.4:1. 8. The pozzolanic cement composition of claim 1, wherein the pozzolanic cement composition is substantially free of citric acid activators, lactic acid activators, alkali metal activators, and metal carbonate activators. 9. The pozzolanic cement composition of claim 3, wherein the retarder comprises 0.1 to 3.0% of the total weight of the pozzolanic cement composition. 10. A pozzolanic cement composition comprising: a pozzolanic material, anda retarder selected from the group consisting of sulfate salts, sugars, sugar acids, lignins, boron compounds or combinations thereof present in an amount of 0.1 to 30% of the total weight of the pozzolanic cement composition, wherein the pozzolanic cement composition has less than 10% by weight Portland cement. 11. The pozzolanic cement composition of claim 10 further comprising an accelerator comprising an amine. 12. The pozzolanic cement composition of claim 10, wherein the accelerator comprises triethanolamine or triisopropanolamine. 13. The pozzolanic cement composition of claim 10, wherein the pozzolanic cement composition is substantially free of Portland cement. 14. The pozzolanic cement composition of claim 10, wherein the pozzolanic cement composition has a set time of between 0.5 hours and 24 hours. 15. The pozzolanic cement composition of claim 10, wherein the pozzolanic material is selected from the group consisting of Class C fly-ash, Class F fly-ash, Class N pozzolanic ash, and combinations thereof. 16. The pozzolanic cement composition of claim 10, wherein the pozzolanic cement composition has a silica to calcia molar ratio of between about 1.2:1 and 1.4:1. 17. The pozzolanic cement composition of claim 10, wherein the pozzolanic cement composition is substantially free of citric acid activators, lactic acid activators, alkali metal activators, and metal carbonate activators. 18. The pozzolanic cement composition of claim 11, wherein the retarder comprises 0.1 to 3.0% of the total weight of the pozzolanic cement composition. 19. A pozzolanic cement composition comprising: a pozzolanic material,an activator or accelerator, anda retarder comprising hepto-gluconate wherein the pozzolanic cement composition has less than 10% by weight Portland cement. 20. The pozzolanic cement composition of claim 19, comprising an activator and an accelerator. 21. The pozzolanic cement composition of claim 19, wherein the retarder further comprises a boron compound. 22. The pozzolanic cement composition of claim 21, wherein the boron compound is selected from the group consisting of boric acid, boric oxide, sodium borate, sodium tetraborate, potassium borate and potassium tetraborate, borax pentahydrate, and borax decahydrate. 23. The pozzolanic cement composition of claim 19, wherein the retarder comprises 0.1 to 3.0% of the total weight of the pozzolanic cement composition. 24. The pozzolanic cement composition of claim 19, wherein the pozzolanic cement composition is substantially free of Portland cement. 25. The pozzolanic cement composition of claim 19, wherein the pozzolanic cement composition has a set time of between 0.5 hours and 24 hours. 26. The pozzolanic cement composition of claim 19, wherein the pozzolan material is selected from the group consisting of Class C fly-ash, Class F fly-ash, Class N pozzolanic ash, and combinations thereof. 27. The pozzolanic cement composition of claim 19, wherein the pozzolanic cement composition has a silica to calcia molar ratio of between about 1.2:1 and 1.4:1. 28. The pozzolanic cement composition of claim 19, wherein the pozzolanic cement composition is substantially free of citric acid activators, lactic acid activators, alkali metal activators, and metal carbonate activators. 29. A method of forming a hardened pozzolanic cement composition comprising: mixing a hydratable composition comprising pozzolanic material,one or more activators or accelerators; anda retarder comprising hepto-gluconate wherein the pozzolanic cement composition has less than 10% by weight Portland cement. 30. The method of claim 29, wherein the retarder further comprises a boron compound. 31. The method of claim 30, wherein the boron compound is selected from the group consisting of boric acid, boric oxide, sodium borate, sodium tetraborate, potassium borate and potassium tetraborate, borax pentahydrate, and borax decahydrate. 32. The method of claim 30, wherein the retarder comprises 0.1 to 3.0% of the total weight of the hardened pozzolanic cement composition. 33. The method of claim 29, wherein the hydratable composition has a set time of between 2 hours and 24 hours after mixing with the activators and hepto-gluconate. 34. The method of claim 29, wherein the hydratable composition comprising pozzolanic material comprises pozzolans selected from the group consisting of Class C fly-ash, Class F fly-ash, Class N pozzolanic ash, and combinations thereof. 35. The method of claim 29, further comprising dissolving the hepto-gluconate in a solution of activator and accelerator in a concentration between 0.1% and 30.0% prior to mixing with the pozzolanic material. 36. The method of claim 29, further comprising dissolving the hepto-gluconate in a solution of activator and accelerator in a concentration between 10.0% and 30.0% prior to mixing with the pozzolanic material.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (15)
Turpin ; Jr. Raymond C. (3825 Wieuca Ter. ; NW. Atlanta GA 30342), Cement compositions containing self-setting pozzolans.
Brook John W. (Mantua OH) Factor David F. (Hiram OH) Kinney Frederick D. (Broadview Hts. OH) McCallen Celeste L. (Wexford PA) Young Andrea M. (Redondo Beach CA), Cementitious compositions.
Buerge Theodor A. (Geroldswil CHX) Maeder Urs (Frauenfeld CHX) Wombacher Franz (Oberwil-Lieli CHX) Marazzani Beat (Zurich CHX), Setting- and hardening-accelerator containing no chloride and nitrite and a method to accelerate the setting and hardeni.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.