The invention relates to inorganic glass sheets coated on both sides thereof, the coating on a first side being formed by at least one hard layer and that on the other side by at least one silver-free durable reflecting layer, and to a process for manufacturing them by deposition of the hard layer v
The invention relates to inorganic glass sheets coated on both sides thereof, the coating on a first side being formed by at least one hard layer and that on the other side by at least one silver-free durable reflecting layer, and to a process for manufacturing them by deposition of the hard layer via a CVD technique and that of the reflecting layer by magnetron vacuum sputtering. The sheets are used for the production of thermal insulating glazing and decorative glazing that reflects visible light.
대표청구항▼
1. A coated inorganic glass sheet comprising: an inorganic glass sheet;a first coating on a first face of the inorganic glass sheet, said first coating comprising at least one pyrolytic layer transparent to visible light; anda second coating on a second face of the inorganic glass sheet, said second
1. A coated inorganic glass sheet comprising: an inorganic glass sheet;a first coating on a first face of the inorganic glass sheet, said first coating comprising at least one pyrolytic layer transparent to visible light; anda second coating on a second face of the inorganic glass sheet, said second coating consisting of in the following sequence starting from the second face of the glass sheet:i) an optional underlayer,ii) an optional additional reflecting layer, andiii) a first reflecting layer,wherein the reflecting layer reflects at least 15% visible light as measured when the first reflecting layer is applied to a clear soda-lime float glass sheet with a thickness of 4 mm according to EN410 (according to EN410 —solid angle of 2°),wherein the reflecting layer is a durable layer deposited by cathode sputtering. 2. The coated inorganic glass sheet of claim 1, wherein the inorganic glass of the glass sheet is a soda-lime-silica glass which is clear or colored. 3. The coated inorganic glass sheet of claim 1, wherein the pyrolitic layer comprises tin oxide doped with fluorine or antimony. 4. The coated inorganic glass sheet of claim 1, wherein the first reflecting layer comprises: a niobium oxide, a tantalum oxide, or a mixture thereof; oran oxide of titanium and at least one oxide of an element selected from the group consisting of Al, Zr, Hf, V, Nb, Ta, Mn, Fe, Co, Ni, Cr, Cu and Si. 5. The coated inorganic glass sheet of claim 4, wherein the first reflecting layer comprises a mixture of titanium oxide and zirconium oxide. 6. The coated inorganic glass sheet of claim 1, wherein the second coating comprises the underlayer, the underlayer comprising a metal oxide, a metal nitride or a metal oxynitride. 7. The coated inorganic glass sheet of claim 6, wherein the underlayer comprises pure tin oxide or a mixture of tin oxide and zinc oxide, such that a content of zinc oxide is up to 50% by weight. 8. The coated inorganic glass sheet of claim 7, wherein the underlayer comprises silicon oxide, nitride or oxynitride. 9. The inorganic glass sheet of claim 1, further comprising the additional reflecting layer, the additional reflecting layer comprising an oxide of tantalum, an oxide of niobium, an oxide of titanium, or a titanium oxynitride with an N/O ratio of less than 10%. 10. A glazing, comprising the coated inorganic glass sheet of claim 1, wherein the glazing is suitable for insulating from heat or cold. 11. The glazing of claim 10, which is suitable for the exterior or interior surfaces of buildings. 12. The coated inorganic glass sheet of claim 1, which is suitable as a glass sheet exterior or interior to a glazing of a door to a domestic electric oven. 13. The coated inorganic glass sheet of claim 1, further comprising the additional reflecting layer, the additional reflecting layer comprising a suboxide of tantalum, a suboxide of niobium, or a suboxide of titanium. 14. The coated inorganic glass sheet of claim 1, wherein the thickness of the reflecting layers is from 15 to 90 nm. 15. The coated inorganic glass sheet of claim 1, wherein the thickness of the reflecting layers is from 30 to 60 nm. 16. The coated inorganic glass sheet of claim 1, wherein the first coating consists of a pyrolytic layer transparent to visible light. 17. A coated inorganic glass sheet, consisting essentially of: an inorganic glass sheet;a pyrolytic layer transparent to visible light on a first face of the inorganic glass sheet; anda second coating on a second face of the inorganic glass sheet, each layer in the second coating deposited by cathode sputtering, and said second coating consisting of in the following sequence starting from the second face of the glass sheet:i) an optional underlayer,ii) an optional additional reflecting layer, andiii) a first reflecting layer,wherein the first reflecting layer reflects at least 15% visible light as measured when the first reflecting layer is applied to a clear soda-lime float glass sheet with a thickness of 4mm according to EN410 (according to EN410 —solid angle of 2°),andwherein the first reflecting layer comprises: a niobium oxide, a tantalum oxide, or a mixture thereof; oran oxide of titanium and at least one oxide of an element selected from the group consisting of Al, Zr, Hf, V, Nb, Ta, Mn, Fe, Co, Ni, Cr, Cu and Si, andwherein the second coating does not comprise a silver containing layer. 18. The coated inorganic glass sheet of claim 17, wherein the first reflecting layer comprises a mixture of titanium oxide and zirconium oxide. 19. The coated inorganic glass sheet of claim 17, wherein the second coating further comprises the underlayer, the underlayer comprising a material selected from the group consisting of pure tin oxide, a mixture of tin oxide and zinc oxide such that a content of zinc oxide is up to 50% by weight, silicon oxide, silicon nitride, and silicon oxynitride. 20. The inorganic glass sheet of claim 17, further comprising the additional reflecting layer, the additional reflecting layer comprising an oxide of tantalum, an oxide of niobium, an oxide of titanium, or a titanium oxynitride with an N/O ratio of less than 10%. 21. A coated inorganic glass sheet, comprising: an inorganic glass sheet;a pyrolytic layer transparent to visible light on a first face of the inorganic glass sheet; anda second coating on a second face of the inorganic glass sheet, each layer in the second coating deposited by cathode sputtering, and said second coating comprising a first reflecting layer,wherein the first reflecting layer reflects at least 15% visible light as measured when the first reflecting layer is applied to a clear soda-lime float glass sheet with a thickness of 4mm according to EN410(according to EN410 —solid angle of 2°),wherein the second coating does not comprise a silver containing layer, andwherein the first reflecting layer satisfies Class B mechanical strength and chemical resistance requirements of EN1096-2.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.