Process for preparing scalenohedral precipitated calcium carbonate
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C01F-011/18
D21H-017/67
D21H-019/38
출원번호
US-0379110
(2013-03-19)
등록번호
US-9428398
(2016-08-30)
우선권정보
EP-12164041 (2012-04-13)
국제출원번호
PCT/US2013/032923
(2013-03-19)
국제공개번호
WO2013/142473
(2013-09-26)
발명자
/ 주소
Wenk, Joe
Saunders, George
Maurer, Marc
Skrzypczak, Mathieu
출원인 / 주소
Omya International AG
대리인 / 주소
Amster, Rothstein & Ebenstein LLP
인용정보
피인용 횟수 :
0인용 특허 :
7
초록▼
The present invention provides a process for preparing a precipitated calcium carbonate product. The process comprises the steps of preparing slaking quick time to obtain slaked lime; and subjecting the slaked lime, without agitation, without prior cooling in a heat exchanger, and in the absence of
The present invention provides a process for preparing a precipitated calcium carbonate product. The process comprises the steps of preparing slaking quick time to obtain slaked lime; and subjecting the slaked lime, without agitation, without prior cooling in a heat exchanger, and in the absence of any additives, to carbonation with carbon dioxide as to produce PCC. The newly prepared product develops better performance thanks to improved resistance during processing.
대표청구항▼
1. A process for preparing precipitated calcium carbonate (PCC) comprising the steps of: (a) slaking quick lime to obtain slaked lime;(b) subjecting the slaked lime, without agitation, without prior cooling in a heat exchanger, and in the absence of any additives, to carbonation with carbon dioxide
1. A process for preparing precipitated calcium carbonate (PCC) comprising the steps of: (a) slaking quick lime to obtain slaked lime;(b) subjecting the slaked lime, without agitation, without prior cooling in a heat exchanger, and in the absence of any additives, to carbonation with carbon dioxide gas to produce PCC; and(c) subjecting the PCC obtained in step (b) to one or more screening, dewatering, dispersion and grinding steps to obtain a PCC product containing 85% or more scalenohedral particles. 2. The process according to claim 1, wherein step (a) is performed at an initial temperature of 85° F. to 120° F. 3. The process according to claim 1, wherein step (a) is performed at an initial temperature of 95° F. to 110° F. 4. The process according to claim 1, wherein the temperature of the reaction in step (a) raises to 180° F. to 210° F. 5. The process according to claim 1, wherein the temperature of the reaction in step (a) raises to 195° F. to 205° F. 6. The process according to claim 1, wherein step (a) is performed with mixing or agitation. 7. The process according to claim 1, wherein slaked lime obtained in step (a) has a solids content of 10 to 20% solids. 8. The process according to claim 1, wherein slaked lime obtained in step (a) has a solids content of 12 to 18% solids. 9. The process according to claim 1, which further comprises subjecting the slaked lime obtained in step (a) to screening. 10. The process according to claim 1, wherein as a result of air cooling, the temperature of the slaked lime obtained in step (a) is reduced by 40° F. to 70° F., prior to carbonation in step (b). 11. The process according to claim 1, wherein the slaked lime obtained in step (a) is not subjected to cooling in a heating exchanger prior to carbonation in step (b). 12. The process according to claim 1, wherein the carbonation reaction in step (b) is conducted at an initial temperature of 130° F. to 160° F. 13. The process according to claim 1, wherein the carbonation reaction in step (b) is conducted at an initial temperature of 135° F. to 145° F. 14. The process according to claim 1, wherein the PCC obtained in step (b) is isolated. 15. The process according to claim 1, wherein in step (c) the PCC is passed through one or more screens to obtain a PCC product. 16. The process according to claim 1, wherein the PCC product contains 85% or more scalenohedral particles. 17. The process according to claim 1, wherein the PCC product contains 90% or more scalenohedral particles. 18. The process according to claim 1, wherein the PCC product contains 95% or more scalenohedral particles. 19. The process according to claim 1, wherein the PCC product has a median particle size (d50) of 2.0 to 3.0 microns. 20. The process according to claim 1, wherein the PCC product has a median particle size (d50) of 2.2 to 2.8 microns. 21. The process according to claim 1, wherein the PCC product has a BET surface area of 4.0 to 7.0 m2/g.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (7)
Mathur Vijay K., High speed manufacturing process for precipitated calcium carbonate employing sequential perssure carbonation.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.