A method of preparing a modified catalyst support comprises preparing a titanium-containing catalyst support material by (i) contacting a catalyst support material with an organic titanium compound, or (ii) co-hydrolyzing a hydrolysable organic titanium compound and Al(OR″)3, with the titanium-conta
A method of preparing a modified catalyst support comprises preparing a titanium-containing catalyst support material by (i) contacting a catalyst support material with an organic titanium compound, or (ii) co-hydrolyzing a hydrolysable organic titanium compound and Al(OR″)3, with the titanium-containing catalyst support material then including Al, wherein all R″ are the same or different and are each an organic group. The titanium-containing catalyst support material is calcined at a temperature above 900° C. to obtain a modified catalyst support which includes more than 1 wt % and less than 3.5 wt % Ti, based on the mass of the catalyst support material in the modified catalyst support, the Ti being present in the form of one or more titanium compounds.
대표청구항▼
1. A method of preparing a catalyst precursor, the method comprising preparing a titanium-containing catalyst support material by(i) contacting a catalyst support material with an organic titanium compound, wherein the catalyst support material is selected from the group consisting of (a) a catalyst
1. A method of preparing a catalyst precursor, the method comprising preparing a titanium-containing catalyst support material by(i) contacting a catalyst support material with an organic titanium compound, wherein the catalyst support material is selected from the group consisting of (a) a catalyst support precursor comprising an aluminium compound which, upon calcination, converts to a catalyst support in the form of one or more aluminium oxides, and (b) a catalyst support being alumina in the form of one or more aluminium oxides, or(ii) co-hydrolysing a hydrolysable organic titanium compound and Al(OR″)3 to form the titanium-containing catalyst support material which includes Al,wherein all R″ are the same or different and are each an organic group;calcining the titanium-containing catalyst support material at a temperature above 900° C. to obtain a modified catalyst support which includes more than 1 wt % and less than 3.5 wt % Ti, based on the weight of the modified catalyst support, the Ti being present in the form of one or more titanium compounds;introducing a precursor compound of cobalt (Co) onto and/or into the modified catalyst support thereby to obtain a catalyst precursor; andintroducing a dopant capable of enhancing the reducibility of the cobalt (Co) onto and/or into the modified catalyst support, the dopant being introduced as a dopant compound which is a compound of a metal selected from the group consisting of palladium (Pd), platinum (Pt), ruthenium (Ru), rhenium (Re) and a mixture of two or more thereof. 2. The method according to claim 1, wherein the Ti wt % in the modified catalyst support is more than 1 and less than 3.0. 3. The method according to claim 1, wherein the preparation of the titanium-containing catalyst support material is by means of the contacting of the catalyst support material with the organic titanium compound, with the catalyst support material being the catalyst support precursor comprising the aluminium compound, and which includes shaping the catalyst support precursor into particulate form before calcination thereof. 4. The method according to claim 3, wherein the organic titanium compound is a titanium compound having only organic groups associated with the titanium thereof, with all of the organic groups being associated with the titanium by means of an oxygen atom. 5. The method according to claim 4, wherein the organic titanium compound is selected from the group consisting of titanium (IV) methoxide; titanium (IV) ethoxide; titanium (IV) propoxide; titanium (IV) isopropoxide; titanium (IV) diisopropoxide bis(acetylacetonate); titanium (IV) 2-ethylhexoxide; titanium (IV) hexoxide; titanium(IV) butoxide and titanium (IV) bis(ammonium lactato) dihydroxide. 6. The method according to claim 1, wherein the preparation of the titanium-containing catalyst support material is by the co-hydrolysis of the hydrolysable organic titanium compound and the Al(OR″)3, with the co-hydrolysis of the hydrolysable organic titanium compound and the Al(OR″)3 being carried out by mixing the hydrolysable organic titanium compound and the Al(OR″)3 and hydrolysing the resultant mixture. 7. The method according to claim 6, wherein the titanium-containing catalyst support material is titanium-containing boehmite. 8. The method according to claim 6, wherein the hydrolysable organic titanium compound is a titanium compound wherein all the groups associated with the titanium are organic groups, with all of the organic groups being associated with the titanium by means of an oxygen atom. 9. The method according to claim 8, wherein the hydrolysable organic titanium compound is selected from the group consisting of titanium (IV) methoxide; titanium (IV) ethoxide; titanium (IV) propoxide; titanium (IV) isopropoxide; titanium (IV) diisopropoxide bis(acetylacetonate); titanium (IV) 2-ethylhexoxide; titanium (IV) hexoxide; titanium(IV) butoxide and titanium (IV) bis(ammonium lactato) dihydroxide. 10. The method according to claim 6, wherein R″ of Al(OR″)3 is an acyl or hydrocarbyl group or is a heterohydrocarbyl group. 11. The method according to claim 1, wherein the calcination of the titanium-containing support material is carried out at a temperature of at least 960° C., but below 1150° C. 12. A method of preparing a catalyst, which includes preparing a titanium-containing catalyst support material by(i) contacting a catalyst support material with an organic titanium compound, wherein the catalyst support material is selected from the group consisting of (a) a catalyst support precursor comprising an aluminium compound which, upon calcination, converts to a catalyst support in the form of one or more aluminium oxides, and (b) a catalyst support being alumina in the form of one or more aluminium oxides, or(ii) co-hydrolysing a hydrolysable organic titanium compound and Al(OR″)3 to form the titanium-containing catalyst support material which includes Al,wherein all R″ are the same or different and are each an organic group;calcining the titanium-containing catalyst support material at a temperature above 900° C. to obtain a modified catalyst support which includes more than 1 wt % and less than 3.5 wt % Ti, based on the weight of the modified catalyst support, the Ti being present in the form of one or more titanium compounds;introducing a precursor compound of cobalt (Co) onto and/or into the modified catalyst support thereby to obtain a catalyst precursor;introducing a dopant capable of enhancing the reducibility of the cobalt (Co) onto and/or into the modified catalyst support, the dopant being introduced as a dopant compound which is a compound of a metal selected from the group consisting of palladium (Pd), platinum (Pt), ruthenium (Ru), rhenium (Re) and a mixture of two or more thereof; andreducing the said catalyst precursor, thereby activating the catalyst precursor and obtaining the catalyst. 13. A hydrocarbon synthesis process which comprises preparing a titanium-containing catalyst support material by(i) contacting a catalyst support material with an organic titanium compound, wherein the catalyst support material is selected from the group consisting of (a) a catalyst support precursor comprising an aluminium compound which, upon calcination, converts to a catalyst support in the form of one or more aluminium oxides, and (b) a catalyst support being alumina in the form of one or more aluminium oxides, or(ii) co-hydrolysing a hydrolysable organic titanium compound and Al(OR″)3 to form the titanium-containing catalyst support material which includes Al,wherein all R″ are the same or different and are each an organic group;calcining the titanium-containing catalyst support material at a temperature above 900° C. to obtain a modified catalyst support which includes more than 1 wt % and less than 3.5 wt % Ti, based on the weight of the modified catalyst support, the Ti being present in the form of one or more titanium compounds;introducing a precursor compound of cobalt (Co) onto and/or into the modified catalyst support thereby to obtain a catalyst precursor;introducing a dopant capable of enhancing the reducibility of the cobalt (Co) onto and/or into the modified catalyst support, the dopant being introduced as a dopant compound which is a compound of a metal selected from the group consisting of palladium (Pd), platinum (Pt), ruthenium (Ru), rhenium (Re) and a mixture of two or more thereof;reducing the said catalyst precursor, thereby activating the catalyst precursor and obtaining the catalyst; andcontacting hydrogen with carbon monoxide at a temperature above 100° C. and a pressure of at least 10 bar with the catalyst, to produce hydrocarbons and, optionally, oxygenates of hydrocarbons.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (6)
Van Berge,Peter Jacobus; Barradas,Sean, Catalysts.
Van Berge, Peter Jacobus; Van De Loosdrecht, Jan; Barradas, Sean, Method of treating an untreated catalyst support, and forming a catalyst precursor and catalyst from the treated support.