초록 ▼

A multilayer laminate for use as a flame barrier in an aircraft comprising (i) a polymeric film layer capable of withstanding a temperature of at least 200 C for at least 10 min, (ii) an adhesive layer having an areal weight of from 2 to 40 gsm capable of activation at a temperature of from 75 to 20

A multilayer laminate for use as a flame barrier in an aircraft comprising (i) a polymeric film layer capable of withstanding a temperature of at least 200 C for at least 10 min, (ii) an adhesive layer having an areal weight of from 2 to 40 gsm capable of activation at a temperature of from 75 to 200 degrees C., (iii) an inorganic refractory layer, and (iv) aramid paper comprising from 50 to 90 weight percent of aramid fibers and from 10 to 50 weight percent of meta-aramid binder wherein the inorganic refractory layer of (iii) comprises platelets in an amount of at least 85% by weight with a dry areal weight of 15 to 50 gsm and a residual moisture content of no greater than 10 percent by weight.

대표청구항 ▼

1. A multilayer laminate for use as a flame barrier in an aircraft comprising (i) a polymeric film layer having a temperature resistance of at least 200 degrees C. for at least 10 minutes,(ii) an adhesive layer having an areal weight of from 2 to 40 gsm having an activation temperature of from 75 to

1. A multilayer laminate for use as a flame barrier in an aircraft comprising (i) a polymeric film layer having a temperature resistance of at least 200 degrees C. for at least 10 minutes,(ii) an adhesive layer having an areal weight of from 2 to 40 gsm having an activation temperature of from 75 to 200 degrees C.,(iii) an inorganic refractory layer having a dry areal weight of 15 to 50 gsm and residual moisture content of no greater than 10 percent by weight, and(iv) aramid paper comprising from 50 to 90 weight percent of aramid fibers and from 10 to 50 weight percent of meta-aramid binder; wherein the inorganic refractory layer of (iii) comprises platelets of vermiculite in an amount of at least 90% by weight. 2. The laminate of claim 1 wherein the inorganic refractory layer is perforated. 3. The laminate of claim 1 wherein the polymeric film layer is a fluoropolymer, polyimide, polyetheretherketone, or polyetherketoneketone. 4. The laminate of claim 1 wherein the polymeric film layer is metalized on at least one surface. 5. The laminate of claim 1 wherein the adhesive layer contains up to 40 weight percent of a flame retardant ingredient. 6. The laminate of claim 1 wherein the adhesion bond between inorganic refractory layer and the polymeric film is at least 0.25 lb/in. 7. The laminate of claim 1 wherein the inorganic refractory layer has a dry areal weight of from 20 to 35 gsm. 8. The laminate of claim 1 wherein the inorganic refractory layer has a moisture content of no greater than 3%. 9. The laminate of claim 2 wherein the inorganic refractory layer comprises platelets of vermiculite in an amount of at least 95% by weight. 10. The laminate of claim 6 wherein the adhesion bond between inorganic refractory layer and the polymeric film is at least 0.8 lb/in. 11. A thermal acoustic blanket for an aircraft comprising (i) a core of fibrous batting having first and second outer surfaces,(ii) a multilayer laminate covering the first outer surface of the core and partially covering the second outer surface of the core, and(iii) a polymeric backing film covering the portion of the second outer surface of the core not covered by the multilayer laminate, wherein,the polymeric backing film overlaps and is bonded to the multilayer laminate,the polymeric backing film can withstand a temperature of at least 200 C for at least 10 min, andthe core has a self- extinguishing time no greater than 10 seconds and a maximum burn length of no greater than 102 mm,wherein the multilayer laminate of (ii) comprises:(a) a polymeric film layer having a temperature resistance of at least 200 C for at least 10 min,(b) an adhesive layer having an dry areal weight of from 2 to 40 gsm having an activation temperature of from 75 to 200 degrees C.,(c) an inorganic refractory layer having a dry areal weight of 15 to 50 gsm and residual moisture content of no greater than 10 percent by weight and comprising platelets of vermiculite in an amount of at least 85% by weight, and(d) aramid paper comprising from 50 to 90 weight percent of aramid fibers and from 10 to 50 weight percent of meta-aramid binder.