A compositional range of high strain point and/or intermediate expansion coefficient alkali metal free aluminosilicate and boroaluminosilicate glasses are described herein. The glasses can be used as substrates or superstrates for photovoltaic devices, for example, thin film photovoltaic devices suc
A compositional range of high strain point and/or intermediate expansion coefficient alkali metal free aluminosilicate and boroaluminosilicate glasses are described herein. The glasses can be used as substrates or superstrates for photovoltaic devices, for example, thin film photovoltaic devices such as CdTe or CIGS photovoltaic devices or crystalline silicon wafer devices. These glasses can be characterized as having strain points ≧600° C., thermal expansion coefficient of from 35 to 50×10−7/° C.
대표청구항▼
1. A glass comprising, in mole percent: 58-62%SiO2; 8-13%Al2O3; 6-12%B2O3; 0-7%MgO; 0-12%SrO; 0-16%CaO; and 2-9%BaO,wherein MgO+CaO+BaO+SrO is greater than 14 to 20 percent, and wherein the glass is substantially free of alkali metal, and wherein the glass is characterized by a liquidus
1. A glass comprising, in mole percent: 58-62%SiO2; 8-13%Al2O3; 6-12%B2O3; 0-7%MgO; 0-12%SrO; 0-16%CaO; and 2-9%BaO,wherein MgO+CaO+BaO+SrO is greater than 14 to 20 percent, and wherein the glass is substantially free of alkali metal, and wherein the glass is characterized by a liquidus temperature of 1150° C. or lower. 2. The glass according to claim 1, comprising 2-11% CaO. 3. The glass according to claim 1, comprising 2-3.6% BaO. 4. The glass according to claim 1, wherein the glass has a liquidus viscosity of 100,000 poise or greater. 5. The glass according to claim 1, wherein MgO+CaO+BaO+SrO is 16 to 20 percent. 6. The glass according to claim 1, having a coefficient of thermal expansion in the range of from about 35×10−7/° C. to about 50×10−7/° C. 7. The glass according to claim 1, comprising 0 to about 2 mole percent of TiO2, MnO, ZnO, Nb2O5, Ta2O5, ZrO2, La2O3, Y2O3, P2O5, or a combination thereof. 8. The glass according to claim 1, wherein the glass is in the form of a sheet. 9. The glass according to claim 1, comprising 62 mole % SiO2. 10. The glass according to claim 1, comprising, in mole percent: 62%SiO2;11.1%Al2O3;10.7%B2O3; 4.6% MgO; 3.6% SrO; 5.4% CaO; and 2.4%BaO. 11. The glass according to claim 1, comprising, in mole percent: 62%SiO2;10.3%Al2O3;10.1%B2O3; 4.2% MgO; 2.9%SrO; 5.6%CaO; and 4.9%BaO. 12. The glass according to claim 1, comprising, in mole percent: 62%SiO2;10.8%Al2O3;10.4%B2O3; 4.4% MgO; 3.3% SrO; 5.5%CaO; and 3.7%BaO. 13. A photovoltaic device comprising the glass according to claim 1.
Gerhard Lautenschlager DE; Klaus Schneider DE; Thomas Kloss DE; Andreas Sprenger DE, Alkali-free aluminoborosilicate glass, its use and process for its preparation.
Danielson, Paul S.; Ellison, Adam J. G.; Venkataraman, Natesan, Glass compositions having high thermal and chemical stability and methods of making thereof.
Ikenishi, Mikio; Morita, Atsuko; Zou, Xuelu, Glass substrate for information recording medium and magnetic information recording medium to which the glass substrate is applied.
Dumbaugh ; Jr. William H. (Painted Post NY) Lapp Josef C. (Corning NY) Moffatt Dawne M. (Corning NY), High liquidus viscosity glasses for flat panel displays.
Harneit,Wolfgang; Jaeger Waldau,Arnulf; Lux Steiner,Martha Christina, Method for producing a solar module with thin-film solar cells which are series-connected in an integrated manner and solar modules produced according to the method, especially using concentrator mod.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.