A removal method of manganese in which manganese is removed by precipitating manganese selectively from sulfuric acid waste water containing aluminum, magnesium and manganese with inhibiting the precipitation of magnesium. The removal method of manganese from waste water in which manganese is remove
A removal method of manganese in which manganese is removed by precipitating manganese selectively from sulfuric acid waste water containing aluminum, magnesium and manganese with inhibiting the precipitation of magnesium. The removal method of manganese from waste water in which manganese is removed by precipitating manganese selectively from the sulfuric acid waste water containing aluminum, magnesium and manganese with inhibiting the precipitation of magnesium, characterized in that said waste water is subjected to the following steps (1) and (2). (1) First, aluminum in said waste water is removed.(2) Subsequently, neutralizing agent is added into the wastewater after removing aluminum, then pH of the waste water is adjusted at 8.0 to 9.0, and oxygen gas is blown.
대표청구항▼
1. A method of removing manganese from a sulfuric acid waste water in which manganese is removed by precipitating manganese selectively from the sulfuric acid waste water containing aluminum, magnesium and manganese, comprising: (1) First, removing aluminum from said sulfuric acid waste water so tha
1. A method of removing manganese from a sulfuric acid waste water in which manganese is removed by precipitating manganese selectively from the sulfuric acid waste water containing aluminum, magnesium and manganese, comprising: (1) First, removing aluminum from said sulfuric acid waste water so that a concentration of aluminum is 0.1 g/L or less;(2) Subsequently, adding neutralizing agent into the sulfuric acid waste water after removing aluminum and adjusting a pH value of the sulfuric acid waste water to no less than 8.0 and less than 9.0; and(3) adding oxygen gas with a purity of 98 volume % or more into the sulfuric acid waste water,wherein manganese is precipitated in steps (2) and (3), andwherein in step (2), the pH value of the sulfuric acid waste water is adjusted to reach an equilibrium by adding neutralizing agent, prior to step (3) of adding the oxygen gas into the sulfuric acid waste water under a pressure load of 0.10 MPa to 0.20 MPa. 2. The method of removing manganese from the sulfuric acid waste water according to claim 1, wherein in step (1) a pH value of the sulfuric acid waste water is adjusted to 4.0 to 6.0 by adding calcium carbonate or calcium hydroxide as a neutralizing agent. 3. The method of removing manganese from the sulfuric acid waste water according to claim 1, wherein a pressurized vessel is used when adding oxygen gas into the sulfuric acid waste water in step (3). 4. The method of removing manganese from the sulfuric acid waste water according to claim 1, wherein said sulfuric acid waste water is obtained from a sulfide precipitation step;wherein the sulfide precipitation step is a step in a hydrometallurgical process in which nickel and cobalt are recovered from nickel oxide ore by High Pressure Acid Leach, comprising a leaching step in which a leach solution is obtained by leaching nickel oxide ore with sulfuric acid; and the sulfide precipitation step in which sulfides of nickel and cobalt are separated and recovered by adding hydrogen sulfide gas into a mother liquid obtained by neutralizing the leach solution. 5. The method of removing manganese from the sulfuric acid waste water according to claim 4, wherein in step (1) a pH value of the sulfuric acid waste water is adjusted to 4.0 to 6.0 by adding calcium carbonate or calcium hydroxide as a neutralizing agent. 6. The method of removing manganese from the sulfuric acid waste water according to claim 4, wherein in step (2), the pH value of the sulfuric acid waste water is adjusted to a range of 8.0 to 9.0 by adding neutralizing agent, prior to step (3) of adding oxygen gas into the sulfuric acid waste water. 7. The method of removing manganese from the sulfuric acid waste water according to claim 4, wherein a pressurized vessel is used when adding oxygen gas into the sulfuric acid waste water in step (3). 8. The method of removing manganese from the sulfuric acid waste water according to claim 1, wherein in step (2), the pH value of the sulfuric acid waste water is adjusted to a range of 8.0 to 9.0 by adding neutralizing agent, prior to step (3) of adding oxygen gas into the sulfuric acid waste water.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (7)
Kobayashi, Hiroshi; Shouji, Hirofumi; Imamura, Masaki; Ozaki, Yoshitomo; Tsuchida, Naoyuki, Hydrometallurgical process of nickel oxide ore.
Burckle,John; Govind,Rakesh; Kawahara,Fred; Scharp,Richard; Tabak,Henry, Process for the purification of acidic metal-bearing waste waters to permissible discharge levels with recovery of marketable metal products.
Misra Manoranjan (Reno NV) Kravetz Mark E. (Cote Madera CA) Yang Kang (Reno NV) McNeel Thomas E. (Memphis TN), Process for the treatment of metal-containing water and recovery of metals therefrom.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.