초록

A basecoat including a pigment blend that includes a ground calcium carbonate component and a hyperplaty clay component, wherein the ground calcium carbonate component has a coarse particle size distribution, and wherein the hyperplaty clay component has an average aspect ratio of at least 40:1.

대표청구항 ▼

1. A method of preparing a basecoat, the method comprising: providing a pigment blend comprising a ground calcium carbonate component and a platy clay component, wherein at most 60 percent of the ground calcium carbonate component has a particle size smaller than 2 microns, wherein the platy clay co

1. A method of preparing a basecoat, the method comprising: providing a pigment blend comprising a ground calcium carbonate component and a platy clay component, wherein at most 60 percent of the ground calcium carbonate component has a particle size smaller than 2 microns, wherein the platy clay component has an average aspect ratio of at least 40:1, and wherein the pigment blend has a sediment void volume of at least 45 percent;providing a carrier; anddispersing the pigment blend in the carrier;wherein the sediment void volume is measured bypreparing a pigment blend sample having the desired weight percentage of the clay component to the calcium carbonate component;diluting the pigment blend sample with water to 50 percent by weight solids to provide a slurry;placing a 70 gram sample of the slurry into a centrifuge tube;spinning the sample at about 8000 g for about 90 minutes;removing the sample from the centrifuge;separating the clear supernatant liquid from the sample;weighing the clear supernatant liquid;determining the weight of water still contained in the voids of the sediment based on the weight of the clear supernatant liquid removed; andusing particle densities, converting the weight of water in the voids into percent sediment void volume. 2. The method of claim 1, comprising the further step of providing at least one additional component and dispersing the at least one additional component in the carrier. 3. The method of claim 2, wherein the at least one additional component is selected from the group consisting of latex, starch, binders, stabilizers, dispersing agents, thickening agents, and additional pigments. 4. The method of claim 1, wherein the carrier comprises water in a quantity sufficient to form a slurry. 5. The method of claim 1 wherein the average aspect ratio of the platy clay component is at least 50:1. 6. The method of claim 1 wherein the average aspect ratio of the platy clay component is at least 70:1. 7. The method of claim 1 wherein the average aspect ratio of the platy clay component is at least 90:1. 8. The method of claim 1 wherein at most 35 percent of the ground calcium carbonate component has a particle size smaller than 2 microns. 9. The method of claim 1 wherein the ground calcium carbonate component is at least 10 percent by weight of the pigment blend and at most 60 percent by weight of the pigment blend. 10. The method of claim 1 wherein the pigment blend consists essentially of the platy clay component and the ground calcium carbonate component. 11. The method of claim 1, wherein the pigment blend has a sediment void volume of at least 47.5 percent. 12. The method of claim 11 wherein the pigment blend has a sediment void volume of at least 50 percent. 13. A method of preparing a basecoat, the method comprising: providing a pigment blend comprising a ground calcium carbonate component and a platy clay component, wherein at most 60 percent of said ground calcium carbonate component has a particle size smaller than 2 microns, wherein the ground calcium carbonate component is at least 25 percent by weight of said pigment blend and at most 60 percent of the pigment blend; wherein said platy clay component has an average aspect ratio of at least 40:1; wherein said pigment blend has a sediment void volume of at least 45 percent; providing a carrier; and dispersing the pigment blend in the carrier; wherein the sediment void volume is measured by preparing a pigment blend sample having the desired weight percentage of the clay component to the calcium carbonate component; diluting the pigment blend sample with water to 50 percent by weight solids to provide a slurry; placing a 70 gram sample of the slurry into a centrifuge tube; spinning the sample at about 8000 g for about 90 minutes; removing the sample from the centrifuge; separating the clear supernatant liquid from the sample; weighing the clear supernatant liquid; determining the weight of water still contained in the voids of the sediment based on the weight of the clear supernatant liquid removed; and using particle densities, converting the weight of water in the voids into percent sediment void volume. 14. The method of claim 13, comprising the further step of providing at least one additional component and dispersing the at least one additional component in the carrier, wherein the at least one additional component is selected from the group consisting of latex, starch, binders, stabilizers, dispersing agents, thickening agents, and additional pigments. 15. The method of claim 13, wherein the carrier comprises water in a quantity sufficient to form a slurry. 16. The method of claim 13, wherein the average aspect ratio of the platy clay component is at least 50:1. 17. The method of claim 13, wherein at most 35 percent of the ground calcium carbonate component has a particle size smaller than 2 microns. 18. The method of claim 13, wherein the ground calcium carbonate component is at least 10 percent by weight of the pigment blend and at most 60 percent by weight of the pigment blend.