Method and apparatus for preparation of granular polysilicon
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C01B-033/027
C23C-016/24
C23C-016/44
C23C-016/442
출원번호
US-0340033
(2014-07-24)
등록번호
US-9764960
(2017-09-19)
우선권정보
KR-10-2006-0075897 (2006-08-10)
발명자
/ 주소
Kim, Hee Young
Yoon, Kyung Koo
Park, Yong Ki
Choi, Won Choon
출원인 / 주소
Korea Research Institute of Chemical Technology
대리인 / 주소
Haug Partners LLP
인용정보
피인용 횟수 :
0인용 특허 :
17
초록▼
A process for preparing granular polysilicon using a fluidized bed reactor is disclosed. The upper and lower spaces of the bed are defined as a reaction zone and a heating zone, respectively, with the height of the reaction gas outlet being selected as the reference height. The invention maximizes t
A process for preparing granular polysilicon using a fluidized bed reactor is disclosed. The upper and lower spaces of the bed are defined as a reaction zone and a heating zone, respectively, with the height of the reaction gas outlet being selected as the reference height. The invention maximizes the reactor productivity by sufficiently providing the heat required and stably maintaining the reaction temperature in the reaction zone, without impairing the mechanical stability of the fluidized bed reactor. This is achieved through electrical resistance heating in the heating zone where an internal heater is installed in a space in between the reaction gas supplying means and the inner wall of the reactor tube, thereby heating the fluidizing gas and the silicon particles in the heating zone. The heat generated in the heating zone is transferred to the reaction zone by supplying the fluidizing gas at such a rate that the silicon particles can be intermixed between the reaction zone and the heating zone in a continuous, fluidized state.
대표청구항▼
1. A method for preparing granular polysilicon using a fluidized bed reactor, which comprises the steps of: forming a bed of silicon particles within a reactor tube, an inner space of which comprises a heating zone and a reaction zone above the heating zone, installed within a reactor shell, wherein
1. A method for preparing granular polysilicon using a fluidized bed reactor, which comprises the steps of: forming a bed of silicon particles within a reactor tube, an inner space of which comprises a heating zone and a reaction zone above the heating zone, installed within a reactor shell, wherein the bed of silicon particles are formed on a fluidizing gas supplying means comprising a gas distribution means that comprises a gas distribution plate and a gas distribution assembly having a plurality of holes and/or nozzles that are arranged to distribute a fluidizing gas at the bottom of the heating zone;providing an internal heater vertically extending from the gas distribution in a space in between a reaction gas supplying means and the inner wall of the reactor tube, wherein the internal heater and the reaction gas supplying means intersect with the gas distribution means, such that the gas distribution plate surrounds the intersection of the internal heater with the gas distribution means, and surrounds the intersection of the reaction gas supplying means with the gas distribution means;performing electrical resistance heating in the heating zone using the internal heater;supplying the fluidizing gas for fluidizing the bed of silicon particles through the fluidizing gas supplying means so that the fluidizing gas is introduced to the bottom of the heating zone through the cross-section of the gas distribution means except for the intersections;supplying a reaction gas for silicon deposition into the bed of silicon particles so that the reaction gas is introduced to the reaction zone through the reaction gas supplying means, wherein an elevation of a reaction gas outlet of the reaction gas supplying means represent a reference height for defining the heating zone and the reaction zone, and for limiting a height of the internal heater within the heating zone; anddischarging an off-gas out of the fluidized bed reactor. 2. The method for preparing granular polysilicon using a fluidized bed reactor as set forth in claim 1, wherein a packed bed is formed in the space in between the reaction gas supplying means and the inner wall of the reactor tube, using packing materials that are not fluidized by the flow of the fluidizing gas. 3. The method for preparing granular polysilicon using a fluidized bed reactor as set forth in claim 1, wherein the fluidizing gas is supplied at such a rate that the silicon particles is intermixed between the reaction zone and the heating zone in a continuously fluidized state, thereby maintaining the reaction temperature of the reaction zone within a predetermined reaction temperature range. 4. The method for preparing granular polysilicon using a fluidized bed reactor as set forth in claim 1, wherein a reaction temperature of the reaction zone is maintained within the range of 600 to 1,200° C. 5. The method for preparing granular polysilicon using a fluidized bed reactor as set forth in claim 1, wherein an inside of the reactor tube is heated by microwave, in addition to the internal heater. 6. The method for preparing granular polysilicon using a fluidized bed reactor as set forth in claim 1, wherein the fluidizing gas is selected from the group consisting of hydrogen, nitrogen, argon, helium, tetrachlorosilane, trichlorosilane, dichlorosilane, hydrogen chloride, and a mixture thereof. 7. The method for preparing granular polysilicon using a fluidized bed reactor as set forth in claim 6, wherein the feeding rate of the fluidizing gas supplied into the heating zone per unit time is 1.0-5.0 times the feeding rate in a minimal fluidized state where the silicon particles begin to be fluidized within a reaction temperature range in the reaction zone without supplying the reaction gas. 8. The method for preparing granular polysilicon using a fluidized bed reactor as set forth in claim 1, wherein the reaction gas is selected from the group consisting of monosilane, dichlorosilane, trichlorosilane, tetrachlorosilane, and a mixture thereof. 9. The method for preparing granular polysilicon using a fluidized bed reactor as set forth in claim 8, wherein the reaction gas further comprises at least one selected from the group consisting of hydrogen, nitrogen, argon, helium, hydrogen chloride, and a mixture thereof. 10. The method for preparing granular polysilicon using a fluidized bed reactor as set forth in claim 1, wherein the silicon seed crystals prepared outside the fluidized bed reactor are supplied into the reactor tube. 11. The method for preparing granular polysilicon using a fluidized bed reactor as set forth in claim 1, wherein an inner space of the reactor shell is divided into an inner zone formed within the reactor tube and an outer zone formed in between the reactor shell and the reactor tube,wherein the bed of silicon particles is present and the reaction zone and the heating zone are comprised in the inner zone while the bed of silicon particles is not present and silicon deposition does not occur in the outer zone. 12. The method for preparing granular polysilicon using a fluidized bed reactor as set forth in claim 11, wherein an inert gas selected from the group consisting of hydrogen, nitrogen, argon, helium, and a mixture thereof is introduced into the outer zone. 13. The method for preparing granular polysilicon using a fluidized bed reactor as set forth in claim 11, wherein the difference of the outer zone pressure (Po) and the inner zone pressure (Pi) is maintained within the range of 0 bar≦|Po−Pi|≦1 bar. 14. The method for preparing granular polysilicon using a fluidized bed reactor as set forth in claim 13, wherein the outer zone pressure or the inner zone pressure is maintained within a range of 1-20 bar.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (17)
Van Slooten Richard A. (E. Aurora NY) Prasad Ravi (E. Amherst NY), Annular heated fluidized bed reactor.
Eichelberger Charles W. (Schenectady NY) Wojnarowski Robert J. (Clifton Park NY), Electrical conductors arranged in multiple layers and preparation thereof.
Kim Hee Y. (Daejeon KRX) Song Yong M. (Daejeon KRX) Jeon Jong Y. (Daejeon KRX) Kwon Dae H. (Daejeon KRX) Lee Kang M. (Daejeon KRX) Lee Jae S. (Daejeon KRX) Park Dong S. (Daejeon KRX), Fluidized bed reactor heated by microwaves.
Kim Hee Y. (Daejeon KRX) Song Yong M. (Daejeon KRX) Jeon Jong Y. (Daejeon KRX) Kwon Dae H. (Daejeon KRX) Lee Kang M. (Daejeon KRX) Lee Jae S. (Daejeon KRX) Park Dong S. (Daejeon KRX), Heating of fluidized bed reactor by microwaves.
Kim, Hee Young; Yoon, Kyung Koo; Park, Yong Ki; Choi, Won Choon, Method for continual preparation of polycrystalline silicon using a fluidized bed reactor.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.