초록 ▼

Embodiments of glass containers resistant to delamination and methods for forming the same are disclosed. According to one embodiment, a delamination resistant glass container may include a glass article having a body extending between an interior surface and an exterior surface. The body defines an

Embodiments of glass containers resistant to delamination and methods for forming the same are disclosed. According to one embodiment, a delamination resistant glass container may include a glass article having a body extending between an interior surface and an exterior surface. The body defines an interior volume. The body may include an interior region extending from 10 nm below the interior surface of the body into a thickness of the body. The interior region has a persistent layer homogeneity such that the body is resistant to delamination.

대표청구항 ▼

1. A delamination resistant glass container comprising: a glass article having a glass body extending between an interior surface and an exterior surface and defining an interior volume, the glass body formed from an aluminosilicate glass having a Class HGA1 hydrolytic resistance when tested accordi

1. A delamination resistant glass container comprising: a glass article having a glass body extending between an interior surface and an exterior surface and defining an interior volume, the glass body formed from an aluminosilicate glass having a Class HGA1 hydrolytic resistance when tested according to the ISO 720 testing standard and comprising: greater than 5 mol. % Al2O3;B2O3 in an amount less than or equal to 0.5 mol. %; andalkaline earth oxides in an amount from 5 mol. % to 8 mol. %; andan interior region extending from about 10 nm below the interior surface of the glass body into a thickness of the glass body and having a persistent layer homogeneity such that the glass body is resistant to delamination and an extrema in the concentration of each constituent component of the aluminosilicate glass in the interior region is greater than or equal to about 80% and less than or equal to about 120% of a bulk concentration of the same constituent component at a mid-point of the thickness of the glass body when the glass container is in an as-formed condition. 2. The glass container of claim 1, wherein the glass article is formed from a glass composition which has a 1000 poise temperature of less than or equal to about 1700° C. 3. The glass container of claim 1, wherein the glass article is formed from a glass composition which is ion-exchangeable. 4. The glass container of claim 1, wherein the interior region has a thickness TLR of at least about 100 nm. 5. The glass container of claim 1, wherein the interior region has a thickness TLR of at least about 200 nm. 6. The glass container of claim 1, wherein the interior region has a thickness TLR of at least about 350 nm. 7. The glass container of claim 1, wherein the interior region has a thickness TLR of at least about 500 nm. 8. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises less than or equal to about 0.3 mol. % of oxides of boron and less than or equal to about 0.3 mol. % of compounds containing boron. 9. The glass container of claim 1, wherein the glass article is formed from a glass composition that is substantially free from boron and compounds containing boron. 10. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises less than or equal to about 0.3 mol. % of oxides of phosphorous or less than or equal to about 0.3 mol. % of compounds containing phosphorous. 11. The glass container of claim 1, wherein the glass article is formed from a glass composition that is substantially free of phosphorous and compounds containing phosphorous. 12. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises less than or equal to about 0.5 mol. % of oxides of zinc or less than or equal to about 0.5 mol. % of compounds containing zinc. 13. The glass container of claim 1, wherein the glass article is formed from a glass composition that is substantially free of zinc and compounds containing zinc. 14. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises less than or equal to about 0.5 mol. % each of, chlorine, fluorine, oxides of tin, compounds containing tin, compounds containing chlorine, or compounds containing fluorine. 15. The glass container of claim 1, wherein the glass article is formed from a glass composition that is substantially free from species which significantly volatilize at temperatures at which the glass composition has a viscosity in a range from about 200 poise to about 100 kilopoise. 16. The glass container of claim 1, wherein the glass container is ion-exchange strengthened. 17. The glass container of claim 1, wherein the glass container comprises a compressive stress greater than or equal to about 300 MPa and a depth of layer greater than or equal to about 10 μm. 18. The glass container of claim 1, wherein the glass container has an ISO Standard 719 hydrolytic resistance of type HGB2 or better. 19. The glass container of claim 1, wherein: the glass body further comprises a surface region extending over the interior surface of the glass container to a depth from about 10 nm to about 50 nm from the interior surface of the glass container; andthe surface region has a persistent surface homogeneity such that the glass body is resistant to delamination and for a discrete point on the interior surface of the glass container, an extrema of the concentration of each constituent component of the aluminosilicate glass in the surface region at the discrete point is greater than or equal to about 70% and less than or equal to about 130% of the same constituent component in the surface region at any second discrete point on the interior surface of the glass container when the glass container is in an as-formed condition. 20. The glass container of claim 19, wherein the glass body has a delamination factor less than or equal to 10. 21. The glass container of claim 19, wherein the glass body has a delamination factor less than or equal to 1. 22. The glass container of claim 1, wherein an extrema in the concentration of each constituent component in the interior region is greater than or equal to about 90% and less than or equal to about 110% of a bulk concentration of the same constituent component at a mid-point of the thickness of the glass body when the glass container is in an as-formed condition. 23. The glass container of claim 1, wherein the glass article is formed from a glass composition which comprises at least one alkali oxide constituent. 24. The glass container of claim 1, wherein the glass body has a delamination factor less than or equal to 10. 25. The glass container of claim 1, wherein the glass container is a pharmaceutical package for containing a pharmaceutical formulation. 26. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises Na2O in an amount greater than or equal to about 9 mol. % and less than or equal to about 13 mol. %. 27. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises K2O in an amount greater than or equal to about 0.01 mol. % and less than or equal to about 2.0 mol. %. 28. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises K2O in an amount greater than or equal to about 0.01 mol. % and less than or equal to about 1.0 mol. %. 29. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises: B2O3 in an amount less than or equal to about 0.5 mol. %; andalkali oxide in an amount greater than 8 mol. %. 30. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises: B2O3 in an amount less than or equal to about 0.5 mol. %; andNa2O in an amount greater than or equal to about 8 mol. %. 31. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises X mol. % of Al2O3 and Y mol. % of alkali oxides, wherein a ratio Y:X is greater than 0.9. 32. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises: SiO2 in an amount greater than or equal to about 67 mol. % and less than or equal to about 78 mol. %; andalkali oxide in an amount greater than 8 mol. %. 33. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises: SiO2 in an amount greater than or equal to about 67 mol. % and less than or equal to about 78 mol. %; andNa2O in an amount greater than or equal to about 8 mol. %. 34. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises: SiO2 in an amount greater than or equal to about 67 mol. % and less than or equal to about 78 mol. %; andX mol. % of Al2O3 and Y mol. % of alkali oxides, wherein a ratio Y:X is greater than 0.9. 35. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises alkali oxides in an amount greater than or equal to about 9 mol. % and less than or equal to about 14 mol. %. 36. The glass container of claim 1, wherein the glass article is formed from a glass composition that comprises greater than or equal to 6 mol. % Al2O3. 37. A delamination resistant glass container comprising: a glass article having a glass body extending between an interior surface and an exterior surface and defining an interior volume, the glass body formed from an aluminosilicate glass having a Class HGA1 hydrolytic resistance when tested according to the ISO 720 testing standard and comprising: greater than 5 mol. % Al2O3;B2O3 in an amount less than or equal to 0.5 mol. %; andalkaline earth oxides in an amount from 5 mol. % to 8 mol. %; andan interior region extending from about 10 nm below the interior surface of the glass body into a thickness of the glass body and having a persistent layer homogeneity such that an extrema in the concentration of each constituent component of the aluminosilicate glass in the interior region is greater than or equal to about 80% and less than or equal to about 120% of a bulk concentration of the same constituent component at a mid-point of the thickness of the glass body when the glass container is in an as-formed condition; andthe glass body has a delamination factor less than or equal to 10. 38. The glass container of claim 37, wherein the glass container is a pharmaceutical package for containing a pharmaceutical formulation. 39. A delamination resistant glass container comprising: a glass article formed from an ion-exchangeable aluminosilicate glass composition having a Class HGA1 hydrolytic resistance when tested according to the ISO 720 testing standard, the glass article having a glass body extending between an interior surface and an exterior surface and defining an interior volume and comprising: greater than 5 mol. % Al2O3;B2O3 in an amount less than or equal to 0.5 mol. %; andalkaline earth oxides in an amount from 5 mol. % to 8 mol. %; andan interior region extending from about 10 nm below the interior surface of the glass body into a thickness of the glass body and having a thickness TLR of at least about 100 nm, wherein an extrema in the concentration of each constituent component of the ion-exchangeable glass composition in the interior region is greater than or equal to about 80% and less than or equal to about 120% of a bulk concentration of the same constituent component at a mid-point of the thickness of the glass body when the glass container is in an as-formed condition. 40. The delamination resistant glass container of claim 39, wherein the glass body has a delamination factor less than or equal to 10. 41. The glass container of claim 39, wherein the glass container is a pharmaceutical package for containing a pharmaceutical formulation. 42. A delamination resistant glass container comprising: a glass article having a glass body extending between an interior surface and an exterior surface and defining an interior volume, the glass body formed from an aluminosilicate glass having a Class HGA1 hydrolytic resistance when tested according to the ISO 720 testing standard and comprising: greater than 5 mol. % Al2O3;B2O3 in an amount less than or equal to 0.5 mol. %; andalkaline earth oxides in an amount from 5 mol. % to 8 mol. %; anda surface region extending over the entire interior surface of the glass container and having a depth extending from the interior surface of the glass container into a thickness of the glass body, the surface region having a persistent surface homogeneity such that the glass body is resistant to delamination and for a discrete point on the interior surface of the glass container, an extrema of the concentration of each constituent component of the aluminosilicate glass in the surface region at the discrete point is greater than or equal to about 70% and less than or equal to about 130% of the same constituent component in the surface region at any second discrete point on the interior surface of the glass container when the glass container is in an as-formed condition. 43. The glass container of claim 42, wherein a depth of the surface region is at least about 10 nm. 44. The glass container of claim 42, wherein a depth of the surface region is at least about 50 nm. 45. The glass container of claim 42, wherein the glass body has a delamination factor less than or equal to 1. 46. The glass container of claim 42, further comprising an interior region extending from about 10 nm below the interior surface of the glass body into a thickness of the glass body and having a persistent layer homogeneity such that the glass body is resistant to delamination and an extrema in the concentration of each constituent component in the interior region is greater than or equal to about 80% and less than or equal to about 120% of a bulk concentration of the same constituent component at a mid-point of the thickness of the glass body when the glass container is in an as-formed condition. 47. The glass container of claim 42, wherein for a discrete point on the interior surface of the glass container, an extrema of the concentration of each constituent component of the glass in the surface region at the discrete point is greater than or equal to about 75% and less than or equal to about 125% of the same constituent component in the surface region at any second discrete point on the interior surface of the glass container when the glass container is in an as-formed condition. 48. The glass container of claim 42, wherein the glass article is formed from a glass composition that comprises less than or equal to about 0.3 mol. % of oxides of boron and less than or equal to about 0.3 mol. % of compounds containing boron. 49. The glass container of claim 42, wherein the glass article is formed from a glass composition that is substantially free from boron and compounds containing boron. 50. The glass container of claim 42, wherein the glass article is formed from a glass composition that comprises less than or equal to about 0.3 mol. % of oxides of phosphorous or less than or equal to about 0.3 mol. % of compounds containing phosphorous. 51. The glass container of claim 42, wherein the glass article is formed from a glass composition that is substantially free of phosphorous and compounds containing phosphorous. 52. The glass container of claim 42, wherein the glass article is formed from a glass composition that comprises less than or equal to about 0.5 mol. % of oxides of zinc or less than or equal to about 0.5 mol. % of compounds containing zinc. 53. The glass container of claim 42, wherein the glass article is formed from a glass composition that is substantially free of zinc and compounds containing zinc. 54. The glass container of claim 42, wherein the glass article is formed from a glass composition that comprises less than or equal to about 0.5 mol. % each of, chlorine, fluorine, oxides of tin, compounds containing tin, compounds containing chlorine, or compounds containing fluorine. 55. The glass container of claim 42, wherein the glass article is formed from a glass composition that is substantially free from species which significantly volatilize at temperatures at which the glass composition has a viscosity in a range from about 200 poise to about 100 kilopoise. 56. The glass container of claim 42, wherein the glass container is ion-exchange strengthened. 57. The glass container of claim 42, wherein the glass article is formed from a glass composition which is ion-exchangeable. 58. The glass container of claim 42, wherein the glass container comprises a compressive stress greater than or equal to about 300 MPa and a depth of layer greater than or equal to about 10 μm. 59. The glass container of claim 42, wherein the glass container has an ISO Standard 719 hydrolytic resistance of type HGB2 or better. 60. The glass container of claim 42, wherein the glass container is a pharmaceutical package for containing a pharmaceutical formulation. 61. A delamination resistant glass container comprising: a glass article having a glass body extending between an interior surface and an exterior surface and defining an interior volume, the glass body formed from an aluminosilicate glass having a Class HGA1 hydrolytic resistance when tested according to the ISO 720 testing standard and comprising: greater than 5 mol. % Al2O3;B2O3 in an amount less than or equal to 0.5 mol. %; andalkaline earth oxides in an amount from 5 mol. % to 8 mol. %; anda surface region extending over the entire interior surface of the glass container and having a depth extending from the interior surface of the glass container into a thickness of the glass body, the surface region having a persistent surface homogeneity such that for a discrete point on the interior surface of the glass container, an extrema of the concentration of each constituent component of the aluminosilicate glass in the surface region at the discrete point is greater than or equal to about 70% and less than or equal to about 130% of the same constituent component in the surface region at any second discrete point on the interior surface of the glass container when the glass container is in an as-formed condition; andthe glass body has a delamination factor less than or equal to 10. 62. The glass container of claim 61, wherein the glass container is a pharmaceutical package for containing a pharmaceutical formulation. 63. A delamination resistant glass container comprising: a glass article formed from an ion-exchangeable aluminosilicate glass composition having a Class HGA1 hydrolytic resistance when tested according to the ISO 720 testing standard, the glass article having a glass body extending between an interior surface and an exterior surface and defining an interior volume and comprising: greater than 5 mol. % Al2O3;B2O3 in an amount less than or equal to 0.5 mol. %; andalkaline earth oxides in an amount from 5 mol. % to 8 mol. %; anda surface region extending over the entire interior surface of the glass container to a depth of about 10 nm from the interior surface of the glass container, wherein, for a discrete point on the interior surface of the glass container, an extrema of the concentration of each constituent component in the surface region at the discrete point is greater than or equal to about 70% and less than or equal to about 130% of the same constituent component in the surface region at any second discrete point on the interior surface of the glass container when the glass container is in an as-formed condition. 64. The glass container of claim 63, wherein the glass container has an ISO Standard 719 hydrolytic resistance of type HGB2 or better. 65. The glass container of claim 63, wherein the glass body has a delamination factor less than or equal to 10. 66. The glass container of claim 63, wherein the glass container is a pharmaceutical package for containing a pharmaceutical formulation. 67. A delamination resistant glass container comprising: a glass article having a glass body extending between an interior surface and an exterior surface, the glass body comprising a wall portion that transitions to a floor portion through a heel portion, the glass body formed from an aluminosilicate glass having a Class HGA1 hydrolytic resistance when tested according to the ISO 720 testing standard and comprising: greater than 5 mol. % Al2O3;B2O3 in an amount less than or equal to 0.5 mol. %; andalkaline earth oxides in an amount from 5 mol. % to 8 mol. %; andan interior region in at least the heel portion of the glass body, the interior region extending from about 10 nm below the interior surface of the glass body into a thickness of the glass body and having a persistent layer homogeneity such that the glass body is resistant to delamination and an extrema in the concentration of each constituent component of the aluminosilicate glass in the interior region is greater than or equal to about 80% and less than or equal to about 120% of a bulk concentration of the same constituent component at a mid-point of the thickness of the glass body when the glass container is in an as-formed condition. 68. The glass container of claim 67, wherein the glass container is a pharmaceutical package for containing a pharmaceutical formulation. 69. A delamination resistant glass container comprising: a glass article having a glass body extending between an interior surface and an exterior surface and comprising a wall portion that transitions to a floor portion through a heel portion, the glass body formed from an aluminosilicate glass having a Class HGA1 hydrolytic resistance when tested according to the ISO 720 testing standard and comprising: greater than 5 mol. % Al2O3;B2O3 in an amount less than or equal to 0.5 mol. %; andalkaline earth oxides in an amount from 5 mol. % to 8 mol. %; anda surface region extending over at least a surface of the heel portion and having a depth extending from the interior surface of the glass container into a thickness of the body, the surface region having a persistent surface homogeneity such that at least the heel portion is resistant to delamination and for a discrete point on the interior surface of the glass container, an extrema of the concentration of each constituent component of the aluminosilicate glass in the surface region at the discrete point is greater than or equal to about 70% and less than or equal to about 130% of the same constituent component in the surface region at any second discrete point on the interior surface of the glass container when the glass container is in an as-formed condition. 70. The glass container of claim 69, wherein the glass container is a pharmaceutical package for containing a pharmaceutical formulation. 71. A method for forming a delamination resistant glass container comprising: providing stock material formed from a delamination resistant aluminosilicate glass composition having a Class HGA1 hydrolytic resistance when tested according to the ISO 720 testing standard, the aluminosilicate glass comprising: greater than 5 mol. % Al2O3;B2O3 in an amount less than or equal to 0.5 mol. %; andalkaline earth oxides in an amount from 5 mol. % to 8 mol. %; andshaping the stock material into a glass article having a glass body extending between an interior surface and an exterior surface and defining an interior volume such that the glass body has an interior region extending from about 10 nm below the interior surface of the glass body into a thickness of the glass body, the interior region having a persistent layer homogeneity such that the glass body is resistant to delamination and an extrema in the concentration of each constituent component of the aluminosilicate glass in the interior region is greater than or equal to about 80% and less than or equal to about 120% of a bulk concentration of the same constituent component at a mid-point of the thickness of the glass body when the glass container is in an as-formed condition. 72. The method of claim 71, wherein the interior region has a thickness TLR of at least about 100 nm. 73. The method of claim 71, wherein the interior region has a thickness TLR of at least about 200 nm. 74. The method of claim 71, wherein the interior region has a thickness TLR of at least about 350 nm. 75. The method of claim 71, wherein the interior region has a thickness TLR of at least about 500 nm. 76. The method of claim 71, wherein the glass body has a delamination factor less than or equal to 10. 77. The method of claim 71, wherein the stock material is shaped such that the glass body further comprises a surface region extending over the entire interior surface of the glass body to a depth of about 10 nm from the interior surface of the glass body and the surface region has a persistent surface homogeneity such that the glass body is resistant to delamination and that for a discrete point on the interior surface of the glass container, an extrema of the concentration of each constituent component of the aluminosilicate glass in the surface region at the discrete point is greater than or equal to about 70% and less than or equal to about 130% of the same constituent component in the surface region at any second discrete point on the interior surface of the glass container when the glass container is in an as-formed condition. 78. The method of claim 71, further comprising ion exchange strengthening the glass article. 79. A method for forming a delamination resistant glass container comprising: providing stock material formed from a delamination resistant aluminosilicate glass composition having a Class HGA1 hydrolytic resistance when tested according to the ISO 720 testing standard, the aluminosilicate glass comprising: greater than 5 mol. % Al2O3;B2O3 in an amount less than or equal to 0.5 mol. %; and alkaline earth oxides in an amount from 5 mol. % to 8 mol. %; and shaping the stock material into a glass article having a glass body extending between an interior surface and an exterior surface and defining an interior volume such that the glass body has a surface region extending over the entire interior surface of the glass body, the surface region having a depth extending from the interior surface of the glass body into a thickness of the glass body and the surface region has a persistent surface homogeneity such that the glass body is resistant to delamination and that for a discrete point on the interior surface of the glass container, an extrema of the concentration of each constituent component of the aluminosilicate glass in the surface region at the discrete point is greater than or equal to about 70% and less than or equal to about 130% of the same constituent component in the surface region at any second discrete point on the interior surface of the glass container when the glass container is in an as-formed condition. 80. The method of claim 79, wherein a depth of the surface region is at least about 10 nm. 81. The method of claim 79, wherein the glass body has a delamination factor less than or equal to 10. 82. The method of claim 79, wherein the stock material is shaped such that the glass body further comprises an interior region extending from about 10 nm below the interior surface of the glass body into a thickness of the glass body, the interior region having a persistent layer homogeneity such that the glass body is resistant to delamination and an extrema in the concentration of each constituent component in the interior region is greater than or equal to about 80% and less than or equal to about 120% of a bulk concentration of the same constituent component at a mid-point of the thickness of the glass body when the glass container is in an as-formed condition.