Sheet metal molding for motor vehicles and process for producing a sheet metal molding for motor vehicles
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
B21D-022/00
B60R-013/02
B21D-022/02
B21D-035/00
C21D-008/04
C21D-009/46
C22C-021/06
C22F-001/047
출원번호
US-0813857
(2011-07-29)
등록번호
US-10029624
(2018-07-24)
우선권정보
EP-10008039 (2010-08-02)
국제출원번호
PCT/EP2011/003822
(2011-07-29)
§371/§102 date
20130201
(20130201)
국제공개번호
WO2012/016667
(2012-02-09)
발명자
/ 주소
Diersmann, Holger
Dörr, Jochen
Grewe, Jochem
Hitz, Andreas
출원인 / 주소
BENTELER AUTOMOBILTECHNIK GMBH
대리인 / 주소
Henry M. Feiereisen LLC
인용정보
피인용 횟수 :
0인용 특허 :
14
초록▼
A motor vehicle sheet metal molding of the invention is produced by hot forming from a metal sheet composed of an aluminum alloy which cannot be precipitation hardened, which contains at least magnesium and optionally manganese in addition to aluminum as alloy component. The motor vehicle sheet meta
A motor vehicle sheet metal molding of the invention is produced by hot forming from a metal sheet composed of an aluminum alloy which cannot be precipitation hardened, which contains at least magnesium and optionally manganese in addition to aluminum as alloy component. The motor vehicle sheet metal molding after forming has, at least locally, degrees of deformation which are above the forming limit curve of the aluminum alloy at room temperature. To produce the motor vehicle sheet metal molding, the metal sheet is heated at least locally to a temperature in the range from 200° C. to 400° C. over a period of from 1 to 60 seconds. The heated metal sheet is subsequently placed in a forming tool of a forming press and formed to produce the motor vehicle sheet metal molding.
대표청구항▼
1. A method for producing an open sheet metal molding comprising the steps of: providing a sheet metal made of a roll hardened, non precipitation-hardenable aluminum alloy comprising aluminum and magnesium, said sheet metal being in a material state defined by a temper designation according to Europ
1. A method for producing an open sheet metal molding comprising the steps of: providing a sheet metal made of a roll hardened, non precipitation-hardenable aluminum alloy comprising aluminum and magnesium, said sheet metal being in a material state defined by a temper designation according to European standard EN515:1993 selected from the group consisting of H12, H14, H16, H18, H19, H22, H24, H26, H28, H32, H34, H36 and H38;heating at least a portion of the sheet metal to a temperature in a range from 250° C. to 370° C. within a time period of 1 to 60 seconds;inserting the heated sheet metal into a forming tool of a forming die;forming the sheet metal into the sheet metal molding; andactively cooling the portion of the sheet metal molding to a temperature below 200° C. within 60 seconds after the heating by placement in a cold forming tool. 2. The method of claim 1, wherein the aluminum alloy further comprises manganese. 3. The method of claim 1, wherein the sheet metal is heated in the heating step to a temperature in a range from 270° C. to 350° C. 4. The method according of claim 1, wherein the portion of the sheet metal has regions which are heated to different temperatures prior to the forming step. 5. The method of claim 1, wherein the portion of the sheet metal has regions which are heated for different respective periods of time. 6. A method for producing an open sheet metal molding comprising the steps of: providing a sheet metal made of a roll hardened, non precipitation-hardenable aluminum alloy comprising aluminum and magnesium, said sheet metal being in a material state defined by a temper designation according to European standard EN515:1993 selected from the group consisting of H12, H14, H16, H18, H19, H22, H24, H26, H28, H32, H34, H36 and H38;heating at least a portion of the sheet metal to a temperature in a range from 250° C. to 370° C. within a time period of 1 to 30 seconds;inserting the heated sheet metal into a forming tool of a forming die;forming the sheet metal into the sheet metal molding; andactively cooling the portion of the sheet metal molding at least locally to a temperature below 200° C. by placement in a cold forming tool, wherein the forming and cooling step are performed within 60 seconds after the heating step.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (14)
Wibbeke, Michael; Handing, Christian; Dörr, Jochen; Lütke-Bexten, Ulrich; Roll, Michael, Bumper for a motor vehicle.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.