Separated treatment of paper substrate with multivalent metal salts and OBAs
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
D21H-021/14
D21H-023/22
D21H-023/56
B05D-001/02
B05D-001/38
B05D-003/12
B05D-005/06
D21H-011/08
D21H-019/10
D21H-019/38
D21H-021/28
D21H-011/14
D21H-017/66
D21H-021/30
출원번호
US-0332589
(2016-10-24)
등록번호
US-10036124
(2018-07-31)
발명자
/ 주소
Skaggs, Benny J.
Brollier, Brian W.
출원인 / 주소
INTERNATIONAL PAPER COMPANY
대리인 / 주소
Barnes, III, Thomas W.
인용정보
피인용 횟수 :
0인용 특허 :
60
초록▼
A process for providing printable substrates by separately treating one or both surfaces of a paper substrate with an optical brightening agent (OBA) and a multivalent metal salt drying agent, where one or both surfaces of the paper substrate is treated with one of these two agents at the size press
A process for providing printable substrates by separately treating one or both surfaces of a paper substrate with an optical brightening agent (OBA) and a multivalent metal salt drying agent, where one or both surfaces of the paper substrate is treated with one of these two agents at the size press, and where the surface(s) is treated with the other of these two agents before or after the size press.
대표청구항▼
1. A process comprising the following steps: (a) for a paper substrate comprising about 10% or less by weight mechanical pulp fibers and having a first surface and a second surface, treating at least one of the first and second surfaces at a size press with one of the following two agents: (1) an op
1. A process comprising the following steps: (a) for a paper substrate comprising about 10% or less by weight mechanical pulp fibers and having a first surface and a second surface, treating at least one of the first and second surfaces at a size press with one of the following two agents: (1) an optical brightening agent; or (2) a multivalent metal salt drying agent, to provide a treated paper substrate having one of the two agents; and(b) before or after the size press, treating the at least one surface of the paper substrate of step (a) with the other of the two agents to provide a printable substrate;(c) wherein the least one surface after steps (a) and (b) comprises the multivalent metal salt drying agent in an amount such that the at least one surface has a black print density value of at least about 1.15;(d) wherein the optical brightening agent is present after steps (a) and (b) in an amount sufficient to impart to the at least one surface an ISO brightness value of at least about 75. 2. The process of claim 1, wherein steps (a) and (b) are carried out on both the first and second surfaces. 3. The process of claim 2, wherein the first and second surfaces are treated with the multivalent metal salt drying agent at a pickup of from about 0.15 to about 3% by weight of the multivalent metal salt drying agent per ton of paper substrate. 4. The process of claim 3, wherein the first and second surfaces are treated with the multivalent metal salt drying agent at a pickup of from about 0.35 to about 1.3% by weight of the multivalent metal salt drying agent per ton of paper substrate. 5. The process of claim 2, wherein the first and second surfaces are treated with the optical brightening agent at a pickup 0.25 to about 3% by weight of the optical brightening agent per ton of paper substrate. 6. The process of claim 5, wherein the first and second surfaces are treated with the optical brightening agent at a pickup of from about 1 to about 2% by weight of the optical brightening agent per ton of paper substrate. 7. The process of claim 1, wherein the multivalent metal salt drying agent comprises one or more of: a calcium salt or a magnesium salt. 8. The process of claim 7, wherein the multivalent metal salt drying agent comprises a calcium salt. 9. The process of claim 8, wherein the calcium salt comprises calcium chloride. 10. The process of claim 1, wherein the multivalent metal salt drying agent is present on the at least one of the first and second surfaces to provide a black print density value of at least about 1.25. 11. The process of claim 10, wherein the multivalent metal salt drying agent is present on the at least one of the first and second surfaces to provide a black print density value of at least about 1.45. 12. The process of claim 1, wherein the multivalent metal salt drying agent present on the at least one of the first and second surfaces to provide an edge acuity (EA) value of less than about 15. 13. The process of claim 12, wherein the multivalent metal salt drying agent is present on the at least one of the first and second surfaces to provide an edge acuity (EA) value of less than about 10. 14. The process of claim 1, wherein the optical brightening agent is present in an amount sufficient to impart an ISO Brightness value of at least about 85. 15. The process of claim 14, wherein the optical brightening agent is present in an amount sufficient to impart an ISO Brightness value of at least about 90. 16. The process of claim 1, wherein the optical brightening agents comprises one or more of: 4,4′-bis-(triazinylamino)-stilbene-2,2′-disulfonic acids, 4,4′-bis-(triazol-2-yl)stilbene-2,2′-disulfonic acids, 4,4′-dibenzofuranyl-biphenyls, 4,4′-(diphenyl)-stilbenes, 4,4′-distyryl-biphenyls, 4-phenyl-4′-benzoxazolyl-stilbenes, stilbenzyl-naphthotriazoles, 4-styryl-stilbenes, bis-(benzoxazol-2-yl) derivatives, bis-(benzimidazol-2-yl) derivatives, coumarins, pyrazolines, naphthalimides, triazinyl-pyrenes, 2-styryl-benzoxazole or -naphthoxazoles, or benzimidazole-benzofurans or oxanilides. 17. The process of claim 16, wherein the optical brightening agent comprises one or more stilbene-based sulfonates. 18. The process of claim 17, wherein these one or more stilbene-based sulfonates comprise derivatives of 4,4′-diaminostilbene-2,2′-disulphonic acid, 4,4-bis(triazine-2-ylamino)stilbene-2,2′-disulphonic acid, disodium salts of distyrlbiphenyl disulfonic acid, or disodium salts of 4,4′-di-triazinylamino-2,2′-di-sulfostilbene. 19. The process of claim 1, wherein the optical brightening agent is present on the at least one of the first and second surfaces in an amount sufficient to impart a CIE Whiteness value of at least about 115. 20. The process of claim 19, wherein the optical brightening agent is present on the at least one of the first and second surfaces in an amount sufficient to impart a CIE Whiteness value of at least about 125. 21. The process of claim 20, wherein the optical brightening agent is present on the at least one of the first and second surfaces in an amount sufficient to impart a CIE Whiteness value of at least about 145. 22. The process of claim 1, wherein step (b) is carried out before step (a). 23. The process of claim 1, wherein step (b) is carried out after step (a). 24. The process of claim 1, wherein step (b) is carried out by spraying the other of the two agents onto the at least one surface of the paper substrate of step (a). 25. The process of claim 23, wherein step (a) is carried out by treating the at least one of the first and second surfaces of the paper substrate with the optical brightening agent, and wherein step (b) is carried out by treating the at least one surface of the paper substrate of step (a) with the multivalent metal salt drying agent. 26. The process of claim 1, wherein step (a) is carried out by treating the at least one of the first and second surfaces of the paper substrate with the multivalent metal salt drying agent, and wherein step (b) is carried out by treating the at least one surface of the paper substrate of step (a) with the optical brightening agent. 27. The process of claim 1, wherein the paper substrate comprises less than about 5% by weight mechanical pulp fibers. 28. The process of claim 27, wherein the paper substrate comprises less than about 1% by weight mechanical pulp fibers. 29. A process comprising the following steps: (a) for a paper substrate comprising greater than about 10% by weight mechanical pulp fibers and having a first surface and a second surface, treating at least one of the first and second surfaces at a size press with one of the following two agents: (1) an optical brightening agent or; (2) a multivalent metal salt drying agent, to provide a treated paper substrate having one of the two agents; and(b) before or after the size press, treating the at least one surface of the paper substrate of step (a) with the other of the two agents to provide a printable substrate;(c) wherein the least one surface after steps (a) and (b) comprises the multivalent metal salt drying agent in an amount such that the at least one surface has a black print density value of at least about 1.15;(d) wherein the optical brightening agent is present after steps (a) and (b) in an amount sufficient to impart to the at least one surface an ISO brightness value of at least about 75. 30. The process of claim 29, wherein steps (a) and (b) are carried out on both the first and second surfaces. 31. The process of claim 30, wherein the first and second surfaces are treated with the multivalent metal salt drying agent at a pickup of from about 0.15 to about 3% by weight of the multivalent metal salt drying agent per ton of paper substrate. 32. The process of claim 31, wherein the first and second surfaces are treated with the multivalent metal salt drying agent at a pickup of from about 0.35 to about 1.3% by weight of the multivalent metal salt drying agent per ton of paper substrate. 33. The process of claim 30, wherein the first and second surfaces are treated with the optical brightening agent at a pickup 0.25 to about 3% by weight of the optical brightening agent per ton of paper substrate. 34. The process of claim 33, wherein the first and second surfaces are treated with the optical brightening agent at a pickup of from about 1 to about 2% by weight of the optical brightening agent per ton of paper substrate. 35. The process of claim 29, wherein the multivalent metal salt drying agent comprises one or more of: a calcium salt or a magnesium salt. 36. The process of claim 35, wherein the multivalent metal salt drying agent comprises a calcium salt. 37. The process of claim 36, wherein the calcium salt comprises calcium chloride. 38. The process of claim 29, wherein the multivalent metal salt drying agent is present on the at least one of the first and second surfaces to provide a black print density value of at least about 1.25. 39. The process of claim 38, wherein the multivalent metal salt drying agent is present on the at least one of the first and second surfaces to provide a black print density value of at least about 1.45. 40. The process of claim 38, wherein the multivalent metal salt drying agent present on the at least one of the first and second surfaces to provide an edge acuity (EA) value of less than about 15. 41. The process of claim 40, wherein the multivalent metal salt drying agent is present on the at least one of the first and second surfaces to provide an edge acuity (EA) value of less than about 10. 42. The process of claim 29, wherein the optical brightening agent is present in an amount sufficient to impart an ISO Brightness value of at least about 85. 43. The process of claim 42, wherein the optical brightening agent is present in an amount sufficient to impart an ISO Brightness value of at least about 90. 44. The process of claim 29, wherein the optical brightening agents comprises one or more of: 4,4′-bis-(triazinylamino)-stilbene-2,2′-disulfonic acids, 4,4′-bis-(triazol-2-yl)stilbene-2,2′-disulfonic acids, 4,4′-dibenzofuranyl-biphenyls, 4,4′-(diphenyl)-stilbenes, 4,4′-distyryl-biphenyls, 4-phenyl-4′-benzoxazolyl-stilbenes, stilbenzyl-naphthotriazoles, 4-styryl-stilbenes, bis-(benzoxazol-2-yl) derivatives, bis-(benzimidazol-2-yl) derivatives, coumarins, pyrazolines, naphthalimides, triazinyl-pyrenes, 2-styryl-benzoxazole or -naphthoxazoles, or benzimidazole-benzofurans or oxanilides. 45. The process of claim 44, wherein the optical brightening agent comprises one or more stilbene-based sulfonates. 46. The process of claim 45, wherein these one or more stilbene-based sulfonates comprise derivatives of 4,4′-diaminostilbene-2,2′-disulphonic acid, 4,4-bis(triazine-2-ylamino)stilbene-2,2′-disulphonic acid, disodium salts of distyrlbiphenyl disulfonic acid, or disodium salts of 4,4′-di-triazinylamino-2,2′-di-sulfostilbene. 47. The process of claim 29, wherein the optical brightening agent is present on the at least one of the first and second surfaces in an amount sufficient to impart a CIE Whiteness value of at least about 100. 48. The process of claim 46, wherein the optical brightening agent is present on the at least one of the first and second surfaces in an amount sufficient to impart a CIE Whiteness value of at least about 105. 49. The process of claim 48, wherein the optical brightening agent is present on the at least one of the first and second surfaces in an amount sufficient to impart a CIE Whiteness value of at least about 115. 50. The process of claim 29, wherein step (b) is carried out before step (a). 51. The process of claim 29, wherein step (b) is carried out after step (a). 52. The process of claim 47, wherein step (b) is carried out by spraying the other of the two agents onto the at least one surface of the paper substrate of step (a). 53. The process of claim 51, wherein step (a) is carried out by treating the at least one of the first and second surfaces of the paper substrate with the optical brightening agent, and wherein step (b) is carried out by treating the at least one surface of the paper substrate of step (a) with the multivalent metal salt drying agent. 54. The process of claim 47, wherein step (a) is carried out by treating the at least one of the first and second surfaces of the paper substrate with the multivalent metal salt drying agent, and wherein step (b) is carried out by treating the at least one surface of the paper substrate of step (a) with the optical brightening agent. 55. The process of claim 29, wherein the paper substrate comprises from about 15 to 100% by weight mechanical pulp fibers. 56. The process of claim 55, wherein the paper substrate comprises from about 50 to 95% by weight mechanical pulp fibers.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (60)
Mackey Larry N. (Fairfield OH) Seyed-Rezai Seyed E. (Fairfield OH), Absorbent paper comprising polymer-modified fibrous pulps and wet-laying process for the production thereof.
Cook Jeffery T. (Memphis TN) Lash Glen R. (Cincinnati OH) Moore Danny R. (Germantown TN) Young Gerald A. (Cincinnati OH), Absorbent structures containing stiffened fibers and superabsorbent material.
Smith David Jay (Montgomery OH) Ruth ; Jr. Jimmie Ed (Forest Park OH), Aldehyde-modified cellulosic fibers for paper products having high initial wet strength.
Barcus Robert Lee (Springfield Township OH) Bjorkquist David William (Wyoming OH), Fibers and pulps for papermaking based on chemical combination of poly (acrylate-co-itaconate), polyol and cellulosic fi.
Barcus Robert L. (Springfield Township OH) Bjorkquist David W. (Wyoming OH), Fibers and pulps for papermaking based on chemical combination of poly(acrylate-co-itaconate), polyol and cellulosic fib.
Barcus Robert L. (Springfield Twp. OH) Bjorkquist David W. (Wyoming OH), Fibers and pulps for papermaking based on chemical combination of poly(acrylate-co-itaconate), polyol and cellulosic fib.
Kroyer Karl K. K. (Le Vieux Moulin ; 12 rue de la Liberation ; 06520 Magagnosc FRX), Method of modifying cellulosic wood fibers and using said fibers for producing fibrous products.
Koukoulas, Alexander A.; Altman, Thomas E.; Matthew, M. C.; Amidon, Thomas E.; Mora, Fernand, Method to manufacture paper using fiber filler complexes.
Barcus Robert L. (Springfield Twp. ; Hamilton County OH) Bjorkquist David W. (Wyoming OH), Poly(methyl vinyl ether-co-maleate) and polyol modified cellulostic fiber.
Frederick Tim J. (Kingsport TN) Mitchell Melvin G. (Kingsport TN) Partin Lee R. (Kingsport TN), Process for preparation of cellulose acetate filters for use in paper making.
Schoen Horst (Bielefeld DEX) Heyer Horst W. (Schwalmtal DEX) Friesen Wolfram (Nettetal-Lobberich DEX), Process for the manufacture of paper webs having CF or CB layers for pressure-sensitive recording.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.