초록 ▼

A method and apparatus for processing a metallic workpiece with defined edges (e.g., a gear) comprises media blasting of the workpiece by directing a first media against exposed surfaces on the workpiece to increase the root strength of the gear, the blasting causing the defined edges to be radiused

A method and apparatus for processing a metallic workpiece with defined edges (e.g., a gear) comprises media blasting of the workpiece by directing a first media against exposed surfaces on the workpiece to increase the root strength of the gear, the blasting causing the defined edges to be radiused or mushroomed, ceasing the media blasting, loading the workpiece into a finishing apparatus, and subjecting the workpiece to a finishing process with a second media, the exposed surfaces on the workpiece being subjected to the finishing process to reduce the radiused edges on the workpiece created from the media blasting. The process of moving the workpiece to the spindle-finishing apparatus from the media blasting may be performed automatically by a machine. Once the workpiece has been subjected to the finishing process with the second media, it may be removed from the spindle-finishing machine, washed, and rinsed with rust inhibitor whereby wear properties of the workpiece are enhanced.

대표청구항 ▼

1. A method of processing a workpiece, the method comprising: forming the workpiece with one or more defined edges, the one or more defined edges having a cross-sectional shape that includes at least one tip;subjecting the workpiece to a media blasting process with a first media, the media blasting

1. A method of processing a workpiece, the method comprising: forming the workpiece with one or more defined edges, the one or more defined edges having a cross-sectional shape that includes at least one tip;subjecting the workpiece to a media blasting process with a first media, the media blasting process forming the tip of the one or more defined edges into a radiused tip, the radiused tip having a first width; andsubjecting the workpiece to a finishing process after the media blasting process, the finishing process comprising vibrating a second media to wear down the radiused tip such that the width of the radiused tip becomes a second width, wherein the second width is less than the first width. 2. The method of claim 1, wherein the workpiece comprises one or more teeth, and wherein the one or more defined edges are located on a tip of the one or more teeth. 3. The method of claim 2, wherein the workpiece is a gear. 4. The method of claim 1, wherein the media blasting process is a peening process. 5. The method of claim 4, wherein the peening process directs a stream of the first media suspended in air toward the workpiece, the workpiece being rotated at a constant rate during processing. 6. The method of claim 1, wherein the finishing process includes a spindle apparatus that retains the workpiece within a processing bowl comprising the second media. 7. The method of claim 6, wherein the spindle apparatus rotates the workpiece within the processing bowl. 8. The method of claim 6, wherein the processing bowl rotates the second media when the workpiece is retailed within the bowl. 9. The method of claim 6, wherein the bowl includes at least one fin to rotate the second media within the bowl. 10. The method of claim 6, wherein the finishing process includes a second spindle apparatus to retain a second workpiece within the processing bowl. 11. The method of claim 1, wherein the first media comprises cut wire, ceramic beads, fine steel beads, or glass beads. 12. The method of claim 1, wherein the second media comprises metal, plastic, glass, or ceramic. 13. The method of claim 1, wherein the second media is a slurry. 14. The method of claim 1, wherein the method further comprises rinsing the workpiece with a rush inhibitor after the finishing process. 15. The method of claim 1, wherein the method further comprises transporting the workpiece from the media blasting process to the finishing process on an automated conveyor system. 16. The method of claim 1, wherein the radiused tip has a mushroomed shape as compared to the shape of the tip before the media blasting.