초록 ▼

The invention relates to a monolithic porous material made of amorphous silica or activated alumina, comprising substantially rectilinear capillary channels that are parallel to one another, wherein: the channels have a substantially uniform cross-section relative to each other,the cross-section of

The invention relates to a monolithic porous material made of amorphous silica or activated alumina, comprising substantially rectilinear capillary channels that are parallel to one another, wherein: the channels have a substantially uniform cross-section relative to each other,the cross-section of each channel is regular over its entire length,the channels pass through the material from end to end,the length of the channels is equal to or more than 10 mm. The invention also relates to an annular, radial or axial chromatographic apparatus, the packing of which consists of at least one said monolithic material. The invention also relates to processes for manufacturing such a monolithic material.

대표청구항 ▼

1. A process for preparing a monolithic porous material based on amorphous silica or activated alumina comprising rectilinear capillary channels parallel to one another, comprising the steps of: providing a bundle of channel precursor fibres whose diameter is equal to the diameter of the capillary c

1. A process for preparing a monolithic porous material based on amorphous silica or activated alumina comprising rectilinear capillary channels parallel to one another, comprising the steps of: providing a bundle of channel precursor fibres whose diameter is equal to the diameter of the capillary channels,forming a porous matrix of amorphous silica or activated alumina around the fibres,eliminating the fibres so as to form the capillary channels extending through the porous matrix. 2. The process of claim 1, wherein the channel precursor fibres comprise an ablative layer of a coating material that is removed during a first fibre elimination treatment step. 3. The process of claim 1, wherein the channel precursor fibres are coated with a spacer before forming the bundle to ensure a minimum thickness of the porous matrix between two adjacent channels. 4. The process of claim 1, wherein the porous matrix of amorphous silica has a proportion of macropores greater than 40% of the total porous volume of the monolithic material, wherein the macropores allow the circulation of a fluid in the monolithic porous material. 5. The process of claim 1, wherein the fibres are formed of a hydrolysable polymer, the fibres are assembled in a bundle, the bundle is immersed in a silica gel precursor solution, the solution being caused to gel around the fibres, and the fibres are eliminated by hydrolysis to soluble species of low molecular weight. 6. The process of claim 1, wherein the channel precursor fibres are metal wires with low melting point coated with a film of silica or activated alumina, assembled in a bundle, the bundle is immersed in a silica gel or activated alumina precursor solution, the solution being caused to gel around the fibres, and the fibres are eliminated by melting and draining the molten liquid outside the monolithic porous material. 7. The process of claim 1, wherein the porous matrix is amorphous silica, and the amorphous silica is reinforced by depositing silica on the surface of its constituent particles, before drying thereof. 8. The process of claim 1, wherein the porous matrix comprises silica gel. 9. A process for preparing a monolithic porous material based on silica gel comprising rectilinear capillary channels parallel to one another, comprising the steps of: providing a bundle of channel precursor fibres whose diameter is equal to the diameter of the capillary channels,forming a porous matrix of silica gel around the fibres, andeliminating the fibres so as to form the capillary channels through the silica gel matrix.