초록 ▼

A polymer composition that can be used to form a melt-extruded film is provided. The polymer composition may contain an olefinic polymer and a transition metal salt. By selectively controlling specific aspects of the polymer and the transition metal salt, as well as the relative concentration of eac

A polymer composition that can be used to form a melt-extruded film is provided. The polymer composition may contain an olefinic polymer and a transition metal salt. By selectively controlling specific aspects of the polymer and the transition metal salt, as well as the relative concentration of each component, the present inventors have discovered that the resulting composition can exhibit a relatively fast oxidation rate, which has been found to improve the adhesion of the composition to a wide variety of substrates.

대표청구항 ▼

1. A melt-extruded film comprising a polymer composition, the polymer composition comprising at least one olefinic polymer in an amount of at least about 50 wt. % of the polymer composition and at least one transition metal salt in an amount of from about 10 to about 1,000 parts per million based on

1. A melt-extruded film comprising a polymer composition, the polymer composition comprising at least one olefinic polymer in an amount of at least about 50 wt. % of the polymer composition and at least one transition metal salt in an amount of from about 10 to about 1,000 parts per million based on the weight of olefinic polymers in the composition, wherein the polymer composition exhibits a heat flow of about 0.7 watts per gram or more after being exposed to an oxygen atmosphere at a temperature of 180° C. for a time period of about 100 minutes or less. 2. The melt-extruded film of claim 1, wherein the olefinic polymer includes a low density polyethylene, high density polyethylene, linear low density polyethylene, propylene homopolymer, propylene copolymer, olefin-diene copolymer, ethylene acrylic acid copolymer or a partially neutralized ionomer thereof, ethylene methacrylic acid copolymer or a partially neutralized ionomer thereof, ethylene methylacrylate copolymer, ethylene ethyl acrylate copolymer, ethylene butyl acrylate copolymer, or a combination thereof. 3. The melt-extruded film of claim 1, wherein the olefinic polymer includes low density polyethylene. 4. The melt-extruded film of claim 1, wherein the olefinic polymer includes an ethylene vinyl acetate polymer. 5. The melt-extruded film of claim 4, wherein the ethylene vinyl acetate polymer has a vinyl acetate content of from about 5 wt. % to about 35 wt. %. 6. The melt-extruded film of claim 4, wherein the ethylene vinyl acetate polymer has a density of from about 0.900 to about 1.00 gram per cubic centimeter as determined in accordance with ASTM D1505-10. 7. The melt-extruded film of claim 1, wherein the transition metal salt contains a multi-valent transition metal cation. 8. The melt-extruded film of claim 7, wherein the cation is iron, manganese, nickel, copper, cobalt, vanadium, chromium, or a combination thereof. 9. The melt-extruded film of claim 1, wherein the transition metal salt contains a carboxylate anion. 10. The melt-extruded film of claim 9, wherein the carboxylate anion is derived from a fatty acid. 11. The melt-extruded film of claim 10, wherein the fatty acid is lauric acid, myristic acid, behenic acid, oleic acid, palmitic acid, stearic acid, ricinoleic acid, capric acid, neodecanoic acid, hydrogenated tallow fatty acid, hydroxy stearic acid, the fatty acids of hydrogenated castor oil, erucic acid, coconut oil fatty acid, or a combination thereof. 12. The melt-extruded film of claim 11, wherein the salt is nickel stearate. 13. The melt-extruded film of claim 11, wherein the salt is cobalt stearate. 14. The melt-extruded film of claim 11, wherein the salt is iron stearate, manganese stearate, or a combination thereof. 15. The melt-extruded film of claim 1, wherein the composition contains a mixture of transition metal salts. 16. The melt-extruded film of claim 15, wherein the mixture contains an iron salt and a manganese salt. 17. The melt-extruded film of claim 1, wherein the composition further contains an antioxidant. 18. The melt-extruded film of claim 17, wherein the antioxidant is a sterically hindered phenol. 19. The melt-extruded film of claim 17, wherein the antioxidant is present in an amount of from about 50 to about 450 parts per million of the composition. 20. The melt-extruded film of claim 1, wherein after being exposed to an oxygen atmosphere at a temperature of 180° C., the composition exhibits an onset of heat flow in about 1 minute or less. 21. The melt-extruded film of claim 1, wherein the composition has a melt flow index of from about 5 to about 30 g/10 min as determined in accordance with ASTM D1238-13 at a temperature of 190° C. and a load of 2.16 kilograms. 22. A composite comprising a substrate that is positioned adjacent to the melt-extruded film of claim 1. 23. A packaging material comprising composite, the composite comprising: a substrate; anda melt-extruded film that is positioned adjacent to the substrate and contains a polymer composition, wherein the polymer composition comprises at least one olefinic polymer in an amount of at least about 50 wt. % of the polymer composition and at least one transition metal salt in an amount of from about 10 to about 1,000 parts per million based on the weight of olefinic polymers in the composition. 24. The packaging material of claim 23, wherein the substrate is a film, fibrous layer, foam layer, metal layer, or a combination thereof. 25. The packaging material of claim 23, wherein the substrate is a film. 26. The packaging material of claim 25, wherein the film is a polyester film. 27. The packaging material of claim 25, wherein the film is corona-treated. 28. The packaging material of claim 23, wherein the substrate is a paper web. 29. The packaging material of claim 23, wherein the peel strength between the film and the substrate is about 30 gf/in or more, as determined using a 90° T-peel test in accordance with ASTM D1876-08 (2015). 30. The packaging material of claim 23, wherein the film is positioned between multiple substrates. 31. A method for forming the composite of claim 23, the method comprising extruding the polymer composition through a die to form a molten film and passing the molten film through a nip formed between two rolls, wherein the film contacts the substrate at the nip. 32. The melt-extruded film of claim 1, wherein the onset of heat flow occurs in about 1 minute or less after being exposed to the oxygen atmosphere. 33. The composite of claim 22, wherein the substrate is a film, fibrous layer, foam layer, metal layer, or a combination thereof. 34. The composite of claim 22, wherein the substrate is a film. 35. The composite of claim 34, wherein the film is a polyester film. 36. The composite of claim 34, wherein the film is corona-treated. 37. The composite of claim 22, wherein the substrate is a paper web. 38. The composite of claim 22, wherein the peel strength between the film and the substrate is about 30 gf/in or more, as determined using a 90° T-peel test in accordance with ASTM D1876-08 (2015). 39. The composite of claim 22, wherein the film is positioned between multiple substrates.