Low temperature carburization under soft vacuum
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C23C-008/20
C23C-008/22
C23C-008/02
출원번호
US-0938916
(2015-11-12)
등록번호
US-10156006
(2018-12-18)
발명자
/ 주소
Williams, Peter C.
Collins, Sunniva R.
Marx, Steven V.
출원인 / 주소
Swagelok Company
대리인 / 주소
Calfee, Halter & Griswold LLP
인용정보
피인용 횟수 :
0인용 특허 :
54
초록▼
Low temperature carburization of stainless steel using acetylene as the carburizing specie is carried out under soft vacuum conditions in the presence of hydrogen or other companion gas. As a result, formation of soot and the undesirable thermal oxide film that normally occurs during low temperature
Low temperature carburization of stainless steel using acetylene as the carburizing specie is carried out under soft vacuum conditions in the presence of hydrogen or other companion gas. As a result, formation of soot and the undesirable thermal oxide film that normally occurs during low temperature carburization is eliminated virtually completely.
대표청구항▼
1. A process for surface hardening a workpiece made from an iron, nickel or chromium based alloy by gas carburization in which the workpiece is contacted with a carburizing gas at an elevated carburization temperature to cause carbon to diffuse into the workpiece surfaces thereby forming a hardened
1. A process for surface hardening a workpiece made from an iron, nickel or chromium based alloy by gas carburization in which the workpiece is contacted with a carburizing gas at an elevated carburization temperature to cause carbon to diffuse into the workpiece surfaces thereby forming a hardened primary surface layer essentially free of carbide precipitates, wherein (1) the carburizing gas contains a carburizing specie comprising an unsaturated hydrocarbon,(2) the partial pressure of the carburizing specie in the carburizing gas is about 0.5 to 20 torr (˜67 to ˜2,666 Pa),(3) the total pressure of the carburizing gas is about 3.5 to 100 torr (˜500 to ˜13,000 Pa),(4) the carburizing gas also contains a companion gas, the companion gas comprising hydrogen, natural gas, propane, another C1-C6 alkane or another saturated hydrocarbon, and(5) the carburization potential of the carburizing gas is changed over the course of the carburization reaction by interrupting the carburization process while maintaining the workpiece at elevated temperature and, in addition, reactivating the workpiece during this interruption by contact with a fluorine containing gas. 2. The process of claim 1, wherein the fluorine containing gas in at least one of HF, NF2 and F2. 3. The process of claim 2, wherein carburization is carried out in a carburization reactor, and further wherein the carburization potential is additionally changed by pulsing the flowrate of the carburizing specie fed to the carburization reactor. 4. A process for producing a surface-hardened, corrosion-resistant stainless steel workpiece exhibiting a shiny metallic appearance without requiring removal of byproduct soot or thermal oxide from the workpiece surfaces, the process comprising contacting the workpiece surfaces with an activating gas comprising a mixture of hydrogen and a fluorine containing gas followed by contacting the workpiece surfaces with a carburizing gas in a carburizing reactor under conditions of time and temperature which are sufficient to cause carbon to diffuse into the workpiece surfaces thereby forming a hardened primary surface layer essentially free of carbide precipitates, wherein (1) the carburizing gas fed to the reactor comprises acetylene and hydrogen,(2) the partial pressure of acetylene in the carburizing gas is about 0.5 to 20 torr (˜67 to ˜2,666 Pa), and(3) the total pressure of the carburizing gas is about 3.5 to 100 torr (˜500 to ˜13,000 Pa). 5. The process of claim 4, wherein the molar ratio of hydrogen to acetylene in the carburizing gas is at least 2:1. 6. The process of claim 5, wherein the fluorine containing gas is at least one of HF, NF3 and F2. 7. The process of claim 4, wherein the fluorine containing gas is at least one of HF, NF3 and F2. 8. The process of claim 7, wherein the workpiece is contacted with the activating gas and the carburizing gas in the same carburization reactor without exposing the workpiece to contact with the atmosphere between contact with the activating gas and the carburizing gas. 9. The process of claim 8, wherein the flowrate to the carburization reactor of at least one of (a) the activating gas and (b) the acetylene in the carburizing gas is pulsed. 10. The process of claim 9, wherein the acetylene content of the carburizing gas to the carburization reactor is pulsed. 11. The process of claim 10, wherein at least one of the duration of the pulse and the frequency of the pulse is shortened from an higher value at in early stages of carburization to a relatively lower value in later stages of carburization so that the carburization potential of the carburization gas decreases over the course of the carburization reaction. 12. The process of claim 4, wherein the carburization potential of the carburizing gas is changed over the course of the carburization reaction by interrupting the carburization process while maintaining the workpiece at elevated temperature and, in addition, reactivating the workpiece during this interruption by contact with a fluorine containing gas. 13. The process of claim 12, wherein the fluorine containing gas is at least one of HF, NF3 and F2. 14. The process of claim 4, wherein the carburization potential is additionally changed by pulsing the flowrate of the carburizing specie fed to the carburization reactor.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (54)
Richey ; II Joseph B. ; Goertzen Gerold G., Apparatus and method for forming oxygen-enriched gas and compression thereof for high-pressure mobile storage utilizatio.
Shibata Kimihiro (Yokosuka JPX) Ike Masahide (Yokohama JPX) Isokawa Kenji (Aichi Prefecture JPX) Takada Katsunori (Nagoya JPX), Manufacturing process for high temperature carburized case harden steel.
Filippov Vladimir I. (ulitsa Marxistskaya ; 5 ; kv. 226 Moscow SUX) Parshin Nikolai I. (ulitsa Zelenodolskaya ; 14 ; korpus 2 ; kv. 16 Moscow SUX) Barabanov Igor V. (prospekt Budennogo ; 28 ; korpus , Method and apparatus for chemical heat treatment of steel parts utilizing a continuous electric furnace.
Fink, Paul J.; Hazel, Brian T.; Govern, Christine; Greene, Joseph M., Method for substrate stabilization of diffusion aluminide coated nickel-based superalloys.
Westeren Herbert W. (Barrington RI) Scotto Vincent (Warwick RI) Gronquist ; Jr. Ernest C. (Providence RI) Taft Donald A. (Orange CA), Method of vacuum carburizing.
Kawka Richard J. (Roselle IL) Herring Daniel H. (Elmhurst IL) Roth Philip (Highland Park IL) Sitko Richard J. (Norwood Park Township ; Chicago County IL), Vacuum carburizing steel.
Juryozawa,Hidetoshi; Yokose,Keiji; Abukawa,Fumitaka; Takahashi,Jun; Ebihara,Hisashi, Vacuum heat treatment furnace and method of and apparatus for measuring carbon concentration in atmosphere having reduced pressure..
※ AI-Helper는 부적절한 답변을 할 수 있습니다.