초록 ▼

A ceramic matrix composite component and methods of making are described herein. The ceramic matrix composite may include a silicon containing matrix and refractory fibers embedded within the silicon containing matrix. The ceramic matrix composite component may further include a silicide layer sandw

A ceramic matrix composite component and methods of making are described herein. The ceramic matrix composite may include a silicon containing matrix and refractory fibers embedded within the silicon containing matrix. The ceramic matrix composite component may further include a silicide layer sandwiched between the silicon containing matrix and the refractory fibers. A method of forming a ceramic matrix composite may include infiltrating a fluid that includes a refractory metal element containing compound into a fiber preform that includes fibers. The method may further include depositing the refractory metal element from the refractory metal element containing compound onto the fibers and forming, from the refractory metal element deposited onto the fibers, a refractory metal silicide.

대표청구항 ▼

1. A method of forming a ceramic matrix composite comprising: prior to infiltrating a fiber preform comprising fibers with a slurry, infiltrating a fluid comprising a refractory metal element containing compound into the fiber preform comprising fibers;depositing the refractory metal element from th

1. A method of forming a ceramic matrix composite comprising: prior to infiltrating a fiber preform comprising fibers with a slurry, infiltrating a fluid comprising a refractory metal element containing compound into the fiber preform comprising fibers;depositing the refractory metal element from the refractory metal element containing compound onto the fibers;forming, from the refractory metal element deposited onto the fibers, a refractory metal silicide by at least exposing the refractory metal element to a silicon vapor; andinfiltrating the fiber preform with the slurry. 2. The method of claim 1, wherein the refractory metal element comprises molybdenum, tungsten, tantalum or a combination thereof. 3. The method of claim 1, wherein the refractory metal element containing compound comprises molybdenum chloride. 4. The method of claim 1, wherein the depositing the refractory metal element comprises forming a refractory metal layer comprising the refractory metal element on the fibers, and wherein the forming the refractory metal silicide comprises forming a refractory metal silicide-containing layer on the fibers. 5. The method of claim 4, wherein the slurry comprises silicon carbide. 6. The method of claim 5, further comprising melt infiltrating the fiber preform with a molten silicon containing metal or alloy after infiltrating the fiber preform with the slurry. 7. The method of claim 6, wherein the refractory metal silicide-containing layer substantially restricts chemical diffusion between the fibers and a silicon containing matrix formed as a result of the melt infiltrating. 8. The method of claim 1, further comprising: wherein infiltrating the fiber preform with the slurry comprises infiltrating the fiber preform with a slurry comprising silicon carbide; andmelt infiltrating the fiber preform with a molten silicon containing metal or alloy,wherein silicon from the silicon containing metal or alloy and the refractory metal element form at least a portion of the refractory metal silicide. 9. The method of claim 1, further comprising forming a refractory metal carbide from the refractory metal element deposited from the refractory metal containing compound prior to forming the refractory metal silicide. 10. The method of claim 9, further comprising melt infiltrating the fiber preform with a molten silicon containing metal or alloy to convert the refractory metal carbide to the refractory metal silicide. 11. A method of forming a ceramic matrix composite, the method comprising: prior to infiltrating a fiber preform comprising fibers with a slurry, infiltrating a fluid comprising a refractory metal element containing compound into the fiber preform;depositing the refractory metal element from the refractory metal element containing compound onto the fibers;forming, from the refractory metal element deposited onto the fibers, a refractory metal silicide by at least exposing the refractory metal element to a silicon vapor;infiltrating the fiber preform with a slurry; andmelt infiltrating the fiber preform with a molten silicon containing metal or alloy. 12. The method of claim 11, wherein the slurry comprises silicon carbide.