초록 ▼

An alternate resin-coated paper material for use in making honeycomb. The alternate resin-coated paper material is made from a paper that contains from 30 to 50 weight percent aramid fibers and from 50 to 70 weight percent of non-aramid fibers. A fire retarded phenolic resin is incorporated into the

An alternate resin-coated paper material for use in making honeycomb. The alternate resin-coated paper material is made from a paper that contains from 30 to 50 weight percent aramid fibers and from 50 to 70 weight percent of non-aramid fibers. A fire retarded phenolic resin is incorporated into the paper to make it self-extinguishing in less than 10 seconds with a self-extinguishing burn length of less than 12 inches when exposed to a 12-second vertical flame in accordance with the vertical burn test requirements set forth in 14 C.F.R. Part 25.583. The fire retarded phenolic resin includes a phenol formaldehyde resin and a phosphorous-containing fire retardant.

대표청구항 ▼

1. A honeycomb for use in making aircraft panels wherein said honeycomb has walls comprising a resin-coated paper material that has a self-extinguishing time of less than 10 seconds and a self-extinguishing burn length of less than 12 inches when exposed to a 12 second vertical flame in accordance w

1. A honeycomb for use in making aircraft panels wherein said honeycomb has walls comprising a resin-coated paper material that has a self-extinguishing time of less than 10 seconds and a self-extinguishing burn length of less than 12 inches when exposed to a 12 second vertical flame in accordance with the vertical burn test requirements set forth in 14 C.F.R. Part 25.583, said resin-coated paper material comprising: a. layer of paper comprising from 30 to 50 weight percent para-aramid fibers and para-aramid pulp, based on the total weight of said paper, and from 50 to 70 weight percent non-aramid fibers and non-aramid pulp, based on the total weight of said paper, said non-aramid fibers being selected from the group consisting of polyester fibers and acrylic fibers and said non-aramid pulp comprising, cellulose fibers; anda fire retarded phenolic resin comprising a phenol formaldehyde resin and a sufficient amount of a phosphorous-containing fire retardant so that said fire retarded phenolic resin contains from 2 to 6 weight percent phosphorous, wherein the amount of said fire retarded phenolic resin in said resin-coated paper material is sufficient to so that said resin-coated paper material has a self-extinguishing time of less than 10 seconds and a self-extinguishing burn length of less than 12 inches when exposed to a 12-second vertical flame in accordance with the vertical burn test requirements set forth in 14 C.F.R. Part 25.583. 2. The honeycomb for use in making aircraft panels according to claim 1 wherein said resin-coated paper material comprises from 40 to 65 weight percent of said fire retarded phenolic resin, based on the total weight of said honeycomb walls. 3. The honeycomb for use in making aircraft panels according to claim 1 wherein said phosphorous-containing fire retardant is a phenoxyphosphazene. 4. The honeycomb for use in making aircraft panels according to claim 1 wherein said phosphorous-containing fire retardant is a phosphonate oligomer. 5. A panel that comprises the honeycomb, according to claim 1 and a face sheet that is bonded to said honeycomb. 6. The honeycomb for use in making aircraft panels according to claim 1 wherein the amount of para-aramid pulp in said paper is from 15 to 35 weight percent, based on the total weight of the para-aramid fibers and para-aramid pulp. 7. The honeycomb for use in making aircraft panels according to claim 6 wherein the amount of non-aramid pulp in said paper is from 15 to 35 weight percent, based on the total weight of the non-aramid fibers and non-aramid pulp. 8. The honeycomb for use in making aircraft panels according to claim 1 wherein the amount of non-aramid pulp in said paper is from 15 to 35 weight percent, based on the total weight of the non-aramid fibers and non-aramid pulp.