A method of selectively controlling the self-sealing ability of a tyre obtained by application of a sealing assembly on a drum and subsequent formation thereon of a precursor of a green tyre inclusive of liner and carcass, followed by shaping, curing and molding. The sealing assembly includes: a sel
A method of selectively controlling the self-sealing ability of a tyre obtained by application of a sealing assembly on a drum and subsequent formation thereon of a precursor of a green tyre inclusive of liner and carcass, followed by shaping, curing and molding. The sealing assembly includes: a self-supporting thermoplastic film of polyamide or polyester and a layer of sealing material possessing viscoelasticity and stickiness features, which is associated with and supported by the self-supporting thermoplastic film. The sealing assembly is easily puncturable by a sharp-pointed element while it maintains such a deformability and stickiness that it helps in the transfer of the sealing material during ejection of the sharp-pointed element and limits the transferred material amount to such an extent that holes bigger than a predetermined value are not sealed.
대표청구항▼
1. A method of selectively controlling the self-sealing ability of a tyre comprising: arranging a sealing assembly on a drum; subsequently,forming a precursor of a green tyre inclusive of at least one liner and a carcass on said sealing assembly; and subsequently,shaping, moulding and curing the com
1. A method of selectively controlling the self-sealing ability of a tyre comprising: arranging a sealing assembly on a drum; subsequently,forming a precursor of a green tyre inclusive of at least one liner and a carcass on said sealing assembly; and subsequently,shaping, moulding and curing the combined sealing assembly and tyre precursor, said sealing assembly comprising: i. a self-supporting thermoplastic film of a polyamide or polyester material; andii. a layer of sealing material possessing viscoelastic and stickiness features, which is associated with and supported by said self-supporting thermoplastic film,wherein said self-supporting thermoplastic film, after curing, has a thickness greater than 5 μm and less than 25 μm,said sealing material comprises 30 phr to 50 phr of an elastomeric block copolymer or a styrene-butadiene elastomer and 40 phr to 60 phr of process oil, andsaid sealing assembly being easily puncturable by a sharp-pointed element while maintaining such a deformability and stickiness that it contributes to transfer of the sealing material during ejection of the sharp-pointed element and limits the transferred amount thereof to such an extent that holes bigger than a predetermined value are not sealed. 2. The method as claimed in claim 1, wherein said self-supporting thermoplastic film comprises a polyamide selected from: nylon 6, nylon 66, nylon 46, nylon 11, nylon 12, nylon 610, nylon 612, nylon 6/66 copolymer, nylon 6/66/610 copolymer, nylon MXD 6, nylon 6T, nylon 6/6T copolymer, nylon 66/PP copolymer, nylon 66/PPS copolymer, and mixtures thereof. 3. The method as claimed in claim 1, wherein said self-supporting thermoplastic film comprises polyester selected from: polybutylene terephthalate, polyethylene terephthalate, polyethylene isophtalate, polybutylene terephthalate/tetramethylene glycol copolymer, polyethylene terephthalate/polyethylene isophthalate copolymer, polyarylate, and polybutylene naphthalate. 4. The method as claimed in claim 1, wherein the self-supporting thermoplastic film has an elongation at yield greater than 5%. 5. The method as claimed in claim 1, wherein the self-supporting thermoplastic film has a yield strength from about 20 MPa to about 60 MPa. 6. The method as claimed in claim 1, wherein the self-supporting thermoplastic film has an ultimate elongation greater than 70%. 7. The method as claimed in claim 1, wherein the self-supporting thermoplastic film has an ultimate tensile strength from about 20 MPa to about 150 MPa. 8. The method as claimed in claim 1, wherein the self-supporting thermoplastic film has such a stress relaxation relative to time, that in 10 seconds following achievement of an imposed elongation of 110% to 150%, the thermoplastic film shows a reduction of at least 20% of stress necessary for maintaining such an imposed elongation. 9. The method as claimed in claim 1, wherein the self-supporting thermoplastic film has such a stress relaxation relative to time that within 300 seconds following achievement of an imposed elongation of 110% to 150%, the thermoplastic film shows a reduction of at least 35% of stress necessary for maintaining such an imposed elongation. 10. The method as claimed in claim 1, wherein said self-supporting thermoplastic film, before shaping, has a thickness smaller than 50 μm. 11. The method as claimed in claim 1, wherein said self-supporting thermoplastic film, before shaping, has a thickness from about 10 μm to about 30 μm. 12. The method as claimed in claim 1, wherein said layer of sealing material, before shaping, has a thickness less than about 6 mm. 13. The method as claimed in claim 1, wherein said layer of sealing material, before shaping has a thickness greater than about 3 mm. 14. The method as claimed in claim 1, wherein the sealing material comprises: 50 phr to 70 phr of a synthetic or natural elastomer material excluding an elastomeric block copolymer or a styrene-butadiene elastomer;30 phr to 50 phr of an elastomeric block copolymer, or a styrene-butadiene elastomer;40 phr to 60 phr of process oil;15 phr to 60 phr of at least one tackiness agent; and1 phr to 40 phr of at least one reinforcing filler. 15. The method as claimed in claim 1, wherein the sealing material comprises: 50 phr to 70 phr of a synthetic or natural elastomer material excluding an elastomeric block copolymer or a styrene-butadiene elastomer;30 phr to 50 phr of an elastomeric block copolymer, or a styrene-butadiene elastomer;50 phr to 60 phr of process oil;20 phr to 40 phr of at least one tackiness agent; and5 phr to 30 phr of at least one reinforcing filler. 16. The method as claimed in claim 1, wherein said sealing layer has a maximum thickness less than about 6 mm and greater than about 2.5 mm. 17. The method as claimed in claim 1, wherein, after curing, said self-supporting thermoplastic film has a resistance to puncturing less than about 30N. 18. The method as claimed in claim 1, wherein, after curing, said self-supporting thermoplastic film has a resistance to puncturing less than about 15N.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (8)
Ochiai, Kiyoshi; Ishikawa, Takeshi, Pneumatic tire and method for manufacturing pneumatic tire.
Masami Takasaki JP; Meishi Tanaka JP; Hisao Anzai JP; Masashi Nakamura JP; Chisato Endo JP, Process oil, process for producing the same and rubber composition.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.