초록

=== 연구개발의 내용 및 범위 === 원료 단량체로 고가인 글리콜리드와 락티드의 대량합성 방법을 확립하였다. 생체흡수성 고분자 PG, PL, PGL의 중합조건으로, 단량체 함량비, 촉매량, 반응시간과 온도, 중합조절제 첨가 등에 따른 효과에 대하여 연구하고 제조된 고분자의 물성을 조사하였다. 이로서 흡수성 봉합사로서 적합한 PG, PL, PGL 고분자의 최적 제조조건을 확립하였다.

Abstract ▼

The optimum polymerization conditions of glycolide and lactide were established to produce the biodegradable polymers of poly(glycolide), PG, poly(lactide), PL and poly(glycolide-colactide), PGL which have adequate properties for synthetic absorbable suture.
The monomers, glycol ide and lactide,

The optimum polymerization conditions of glycolide and lactide were established to produce the biodegradable polymers of poly(glycolide), PG, poly(lactide), PL and poly(glycolide-colactide), PGL which have adequate properties for synthetic absorbable suture.
The monomers, glycol ide and lactide, were synthesized by pyrolysis of low molecular weight polymers which were prepared from the condensation of glycolic acid and lactic acid with the catalyst of antimony trioxide. Pyrolysis was carried out at 275℃ for glycol ide and 200℃ for lactide under 2mmHg pressure with a yield of 85%.

목차 Contents

• 표지...1
• 제출문...2
• 요약문...3
• SUMMARY...6
• CONTENTS...9
• 목차...11
• 제1장 서론...13
• 제2장 수술용 봉합사의 종류와 성질...14
• 제 1 절 봉합사의 종류...14
• 제 2 절 봉합사의 기계적 성질과 소독특성...16
• 제 3 절 봉합사의 조직 반응성...17
• 제 4 절 봉합사의 생체 분해성...18
• 제3장 합성 흡수성 봉합사의 제조와 물성...20
• 제4장 실험...25
• 제 1 절 시약 및 기기...25
• 제 2 절 흡수성 봉합사의 분석...26
• 제 3 절 원료 단량체의 제조...28
• 제 4 절 중합체의 제조...33
• 제5장 결과 및 고찰...37
• 제 1 절 글리콜리드의 중합조건 확립...37
• 제 2 절 락티드의 중합조건 확립...40
• 제 3 절 공중합체 PGL의 제조조건 확립...46
• 제 4 절 글리콜산이 중합에 미치는 영향...53
• 제6장 결론...57
• 참고문헌...59
• 부록...61