초록
▼

1. 결합재 제조 공정 및 특성 분석
${\cdot}$최적 조성: ACP319: $Al(OH)_3:CrO_3:H_3PO_4$,(％)=3:1:9 in mol
${\cdot}$...

1. 결합재 제조 공정 및 특성 분석
${\cdot}$최적 조성: ACP319: $Al(OH)_3:CrO_3:H_3PO_4$,(％)=3:1:9 in mol
${\cdot}$가교온도; ＜$200^{\circ}C$ ${\cdot}$내열성; ＜5wt％ loss to $1000^{\cird}C$${\cdot}$내흡습성; <1wt％
${\cdot}$결정화정도; $500^{\circ}C$까지 무정형
2. 최적 Matrix Solution 제조
Cr-Free 친환경성 matrix의 최적조성비 도출
${\cdot}$ $AP:Al_2O_3:AlN/NH_4F/MgO$중 택일 = 100:100:3 in wt
${\cdot}$ $AP:Al_2O_3:AlN : Cu_2O:MgO:Cr_2O_3$ = 100:80:10:5:1:5
${\cdot}$ $AP:Al_2O_3:AlN:CuO:Cr_2O_3$= 100:80:10:5:5
3. 복합재 제조 공정 확립
a. 액상결합재 AS 제조
b. Matrix solution 제조(AP＋filler＋ 첨가제)
c. pre-pragging: 섬유($25{\times}24mm^2$)
d. 적충 성형공정: prep 10장 layer-up
e.가교공정: 가교온도/시간: $170∼200^{\circ}C$ fer 2h at $10∼30^{\circ}C$/hr, 가압공정, $4㎏/cm^2$ for 30min,
f. 섬유강화 복합재(강도, 열전도도)
4. 복합재 특성 분석
＊ACP319 열전도도1.03, 휨강도132㎫, 밀도2.26
${\cdot}$단일 첨가제 matrix 복합재; 밀도($2.0∼2.5g/cm^3$), 휨강도(65∼74㎫), 열전도도(0.6∼1.1W/mK),
${\cdot}$복합 첨가제 matrix 복합재; 밀도($2.1∼2.4g/cm^3$), 휨강도(40∼95㎫), 열전도도(0.9∼l.0W/mK)
5. 복합재 고온특성평가
${\cdot}$ 복합재 최적조성: Matrix(AP+복합첨가제 조성 1)
${\cdot}$ nextel440 복합재; 휨강도(100∼106㎫),${\cdot}$ 유리섬유 복합재; 휨강도(61∼95㎫)
${\cdot}$ nextel312복합재; 휨강도(55∼76㎫)
${\cdot}$ 고온노출시:$500^{\circ}C$ (52.3% 강도저하), $800^{\circ}C$ (43.8% 강도저하)
${\cdot}$ 섬유의 $B_2O_3$ 함유량이 감소할수록 복합재의 강도 우수

Abstract
▼

A. The development of liquid binder for composite
·Optimized ratio; ACP319 [Al(OH)3:CrO3:H3P04(85%)=3:1:9 in mole] *filler:Al2O...

A. The development of liquid binder for composite
·Optimized ratio; ACP319 [Al(OH)3:CrO3:H3P04(85%)=3:1:9 in mole] *filler:Al2O3
·Properties;-Curing temperature;<170℃, -thermal resistance;<5wt% loss to 1000℃.
-hygroscopic resistance;B. Founding the process of Composite
· Preparation of Cr-free Composite: AIN, MgO, CuO, CU20, NH4F
· Founding the process of Composite: Evaluating the processing parameter
· Similar property with ACP319 composite: flexural strength(40~95MPa), thermal conductivity(0.6~1.1W/mK), density(2.0~2.5g/cm3)
C. The optimized Process for composite
· Optimized ratio of composite: Matrix(AP+combinational additive 1)
· Reinforced fiber: aluminoborosilicate(3M, Nextel)
D. High temperature Properties of Binder
*ACP319 Thermal conductivity1.03, flexural strength132MPa, Density2.26
· nexte1440 Composite; flexural strength(1OO~106MPa),
· Glass fiber composite; flexural strength(61~95MPa)
· nexte1312 Composite; flexural strength(55~76MPa)
· Exposure to air at high temperature:500℃(52.3% Reduction of Strength), 800℃(43.8% Reduction of Strength)
· Strength of Composite increase with the higher amount of B203 in Fiber

목차
Contents
▼

• 표지...1
• 제출문...2
• 보고서 초록...3
• 요약문...4
• SUMMARY...6
• CONTENTS...8
• 목차...9
• 제 1 장 연구개발과제의 개요...10
• 1. 기술적 측면...10
• 2. 경제.산업적 측면...11
• 3. 사회.문화적 측면...11
• 제 2 장 국내외 기술개발 현황...12
• 1. 지금까지의 연구 개발 현황...12
• 2. 현 기술상태의 취약성...12
• 3. 앞으로의 전망...12
• 제 3 장 연구개발 수행 내용 및 결과...13
• 1. 서론...13
• 2. 이론적, 실험적 접근 방법...14
• 3. 연구수행 내용 및 결과...15
• 제 4 장 연구개발목표 달성도 및 대외기여도...27
• 1. 연구개발의 최종 목표...27
• 2. 단위 과제별 연구개발 목표...28
• 3. 세부연구목표 및 평가의 착안점...28
• 4. 연구성과 및 목표의 달성도...29
• 제 5 장 연구개발결과의 활용계획...30
• 1. 연구개발의 활용계획...30
• 2. 연구 개발의 파급효과...31
• 제 6 장 연구개발과점에서 수집한 해외과학기술정보...31
• 제 7 장 참고문헌...32
• 특정연구개발사업 연구결과 활용계획서...33
• [첨부1]. 연구결과 활용계획서...34
• [첨부2]. 기술 요약서...39

연구자의 다른 보고서

참고문헌

• 전체(0)
• 논문(0)
• 특허(0)
• 보고서(0)