The effects of alloying elements on the structure and mechanical properties of compacted/vermicular graphite cast irons containing copper, tin and molubdenum for producing pearlite matrix, and also containing phosphorus and boron for increasing wear resistance, were investigated. The Brinell hardnes...

The effects of alloying elements on the structure and mechanical properties of compacted/vermicular graphite cast irons containing copper, tin and molubdenum for producing pearlite matrix, and also containing phosphorus and boron for increasing wear resistance, were investigated. The Brinell hardness and ultimate tensile strength of the specimens with the range of compositions, [1.5% Cu-0.05% Sn-(0.2-0.4)% Mo-(0.2-0.6)% P-(0.035-0.070)% B], was found to fall within in the following range, depending on their composition; Brinell hardness of BHN 250-315, ultimate tensile strength of $28.1-40.3kg/mm^2$. It was also found within this experiment that CV graphite cast irons possessing higher amount of phosphide eutectic exhibit better wear resistance, but the wear resistance became deteriorate when the area fraction of phosphide eutectics exceed more than 10%. From these experimental results, it could be concluded that the CV graphite cast iron containing 1.5% Cu, 0.05% Sn, 0.4% Mo, 0.2% P and 0.035% B showed good mechanical and wear resistance properties.