The effect of DCCA (Drying Control Chemical Additives) on the drying of gel was investigated in order to determine an optimum drying condition of mullite precursor through sol-gel process. Aluminium sec-butoxide was synthesized from aluminium foil and then mullite powders were synthesized from Tetra...

The effect of DCCA (Drying Control Chemical Additives) on the drying of gel was investigated in order to determine an optimum drying condition of mullite precursor through sol-gel process. Aluminium sec-butoxide was synthesized from aluminium foil and then mullite powders were synthesized from Tetra-ethyl-ortho-silicate (TEOS) and the aluminium sec-butoxide. N, N-dimethyl formamide (DMF), Glycerol, 1, 4-Dioxane, and Oxalic acid were used as DCCA. Mullite powders that were calcined at 200, 900, 1100, and $1250^{\circ}C$ for 2hr were analysed by XRD, TG-DTA, FT-IR, and SEM in order to investigate structural change and characteristics of calcined powders. The results of this work showed that the drying time of gel was reduced to about half in the presence of 0.1mol DMF compared with the absence of DCCA and also calcined powders were obtained without remarkable structural change despite of the addition of DCCA.