The synthesis of kaolinite mineral from domestic diatomite for silica resource, commercial vailable gibbsite or alumina for alumina resource were made under various hydrothermal treatment, and the sythetic effect of acidic mineralizers, temperature treatment with time duration, particle size of ...
The synthesis of kaolinite mineral from domestic diatomite for silica resource, commercial vailable gibbsite or alumina for alumina resource were made under various hydrothermal treatment, and the sythetic effect of acidic mineralizers, temperature treatment with time duration, particle size of alumina on formation of kaolinite mineral and the plastic properties of synthesized kaolinite were investigated. The various acidic mineralizers which are HCl, HNO3, H2SO4 and Oxalic acid were employed for hydrothermal reaction in the range of 0.01 mol/ι to 2 mol/ι concentration of each mineralizers. It was found that HCl in the level of 1 mol/ι solution produced highly yields of well-crystallized and platy form kaolinite mineral and gave the most effective extraction of iron oxide, compared to that of others, that HNO3 produced highly yield of kaolinite but lower extraction of iron oxide, that H2SO4 produced low yield of kaolinite and formed alunite mineral, and that oxialic acid formed spherical crystalline kaolinite and gave low extraction of iron oxide. Moreover, it showed that kaolinite minerals were well synthesized in a wide range of less than 2 mol/ι acids, but were poorly synthesized at more than 2 mol/ι acids. However, boehmite and kaolinite were coexistently formed in the temperature range of 18$0^{\circ}C$ and 20$0^{\circ}C$ when the calcined diatomite and gibbsite were involved. The well-ordered kaolinite mineral as a platy form was highly synthesized in the temperature range of 220 and 24$0^{\circ}C$, when the same marterials as above were used with treatment of 1 mol/ι HCl solution. The results also revealed that the size of crystalline platy form kaolinite, synthesized from alumina and calcined diatomite with treatment in 1 mol/ιHCl solution at 24$0^{\circ}C$, was much larger than that of gibbsite and calcined diatomite shown previously, and that kaolinite and corundum minerals were coexistently formed under any hydrothermal treatment conditions. The plasticity of synthesized kaolinite from under 2 ${\mu}{\textrm}{m}$ alumina and calcined diatomite was very poor, and that of the synthesized kaolinite from raw diatomite and gibbsite gave higher than that of calcined diatomite and gibbsite.
The synthesis of kaolinite mineral from domestic diatomite for silica resource, commercial vailable gibbsite or alumina for alumina resource were made under various hydrothermal treatment, and the sythetic effect of acidic mineralizers, temperature treatment with time duration, particle size of alumina on formation of kaolinite mineral and the plastic properties of synthesized kaolinite were investigated. The various acidic mineralizers which are HCl, HNO3, H2SO4 and Oxalic acid were employed for hydrothermal reaction in the range of 0.01 mol/ι to 2 mol/ι concentration of each mineralizers. It was found that HCl in the level of 1 mol/ι solution produced highly yields of well-crystallized and platy form kaolinite mineral and gave the most effective extraction of iron oxide, compared to that of others, that HNO3 produced highly yield of kaolinite but lower extraction of iron oxide, that H2SO4 produced low yield of kaolinite and formed alunite mineral, and that oxialic acid formed spherical crystalline kaolinite and gave low extraction of iron oxide. Moreover, it showed that kaolinite minerals were well synthesized in a wide range of less than 2 mol/ι acids, but were poorly synthesized at more than 2 mol/ι acids. However, boehmite and kaolinite were coexistently formed in the temperature range of 18$0^{\circ}C$ and 20$0^{\circ}C$ when the calcined diatomite and gibbsite were involved. The well-ordered kaolinite mineral as a platy form was highly synthesized in the temperature range of 220 and 24$0^{\circ}C$, when the same marterials as above were used with treatment of 1 mol/ι HCl solution. The results also revealed that the size of crystalline platy form kaolinite, synthesized from alumina and calcined diatomite with treatment in 1 mol/ιHCl solution at 24$0^{\circ}C$, was much larger than that of gibbsite and calcined diatomite shown previously, and that kaolinite and corundum minerals were coexistently formed under any hydrothermal treatment conditions. The plasticity of synthesized kaolinite from under 2 ${\mu}{\textrm}{m}$ alumina and calcined diatomite was very poor, and that of the synthesized kaolinite from raw diatomite and gibbsite gave higher than that of calcined diatomite and gibbsite.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.