초록

용어보기논문에서 용어와 풀이말을 자동 추출한 결과로, 시범 서비스 중입니다. AI-Helper

Abstract ▼ AI-Helper

The relationship between microstructures and tensile properties depending on various solution treatment temperature and cooling rate of Ti-6A1-4V alloy have been investigated. The complex and random edge shaped $\alpha$ phases were formed after the 1st solution treatment at $\beta$

The relationship between microstructures and tensile properties depending on various solution treatment temperature and cooling rate of Ti-6A1-4V alloy have been investigated. The complex and random edge shaped $\alpha$ phases were formed after the 1st solution treatment at $\beta$ region and the 2nd solution treatment at $900^{\circ}C$, which was followed by furnace cooled. When the specimen was subjected to the 2nd solution treated at $950^{\circ}C$, and furnace cooled, $\alpha$ phase changed its morphology to equiaxed structure. The aspect ratio showing the appreciation basis of microstructual refinement decreases with the temperature of 1st and 2nd solution treatment. The slightly decrease in strength were observed in the Widmanstltten structures than in the bimodal structures. Also, ductility of the Widmanstatten structures was considerable lower than that of bimodal structures. The tensile-fractured surface of the Widmanstatten structures appears to be quasi-cleavage and dimple fracture, while that of the bimodal structures was the type of ductile fracture. The tensile fracture surface of the bimodal structures can easily be separated into cental crack areas lying generally perpendicular to the tensile axis and shear lip areas lying at angles of high shear(around 45 deg.) to the tensile axis.