Tungsten thin film was deposited on p-(100) silicon substrate by using the LPCVD(low pressure chemical vapor deposition) technique. $WF_6$ was used as a source gas for tungsten and $SiH_4$ was used as a reducing gas for $WF_6$. Tungsten thin film was deposited by eit...

Tungsten thin film was deposited on p-(100) silicon substrate by using the LPCVD(low pressure chemical vapor deposition) technique. $WF_6$ was used as a source gas for tungsten and $SiH_4$ was used as a reducing gas for $WF_6$. Tungsten thin film was deposited by either SiH4 or Si substrate reduction of $WF_6$ under cold-wall condition and it was deposited by $SiH_4$ reduction of $WF_6$ under hot-wall condition. The crystal structure of deposited thin film under both conditions were identified to be bcc (body centered cubic). The physical and electrical properties of deposited thin films were investigated. The deposited film under hot-wall condition changed to $WSi_2$ film by the annealing under $800^{\circ}C.$ From the experimental results and theoretical considerations, the change of the crystal structure of the thin film by annealing was discussed. $WSi_2$ thin film, which was known to have good compatibility with Si substrate, could be produced under hot-wall condition although the film properties were superior under cold-wall condition.