Abstract ▼ AI-Helper

The growth mechanism of diamond thin films, deposited by Hot Filament CVD, was investigated through observation of changes in their surface morphology as a function of the substance temperature and deposition time. Amorphous carbon or DLC thin films were deposited at low substrate temperature. Diamo...

The growth mechanism of diamond thin films, deposited by Hot Filament CVD, was investigated through observation of changes in their surface morphology as a function of the substance temperature and deposition time. Amorphous carbon or DLC thin films were deposited at low substrate temperature. Diamond films consisting of square-shaped particles, whose surfaces are (100) planes, were deposited at an intermedate temperature. At high substrate temperatures, diamond films consisting of the particles showing both (100) and (111) plane were deposited. The (100) proferred orientation of the diamond films are believed to be due to a relatively high supersaturation during deposition, and the growth condition for the diamond films having (100) preferred orientation can be applied to the single crystal growth since no twins are generated on the (100) plane. The grain size of the diamond films did not change with increasing temperature and its increasing rate with increasing deposition time was the same irrespective of the substrate temperature. However, the nucleation density increased with substrate temperature and its increasing rate with deposition time was much higher for the films deposited at higher substrate temperature.