Dielectric properties were investigated at Mn doped $(Pb_{1-x}Ca_{x})ZrO_{3}$ with x=0.38 in microwavefrequencies. Both the density and Q values of sintered ceramics increased with increasing calciningtemperature. In the sample sintered at $1300^{\circ}C$ for 2 hrs, the deped M...

Dielectric properties were investigated at Mn doped $(Pb_{1-x}Ca_{x})ZrO_{3}$ with x=0.38 in microwavefrequencies. Both the density and Q values of sintered ceramics increased with increasing calciningtemperature. In the sample sintered at $1300^{\circ}C$ for 2 hrs, the deped Mn ions completely solubled in $(Pb,Ca)ZrO_{3}$ phase until 0.5wt% and the grain size was independent of doping amount. It was observed thathigh dielectric constant of 90 - 100 and high quality factor of 1300 at 4 GHz for O.l5wt% Mn doped$(Pb_{0.62}Ca_{0.38})ZrO_{3}$. The Mn" and Mn" worked as acceptors in $(Pb,Ca)ZrO_{3}$ which created the oxygen vacancies and affected the increment of the Q values. However, the excess Mn doping more than 0.5wt% resulted in decreasing Q values.decreasing Q values.