The diffusion barrier property of 100-nm-thick titanium nitride (TiN) film between Cu and Si was investigated using sheet resistance measurements, etch-pit observation, x-ray diffractometry, Auger electron spectroscopy, and transmission electron microscopy. The TiN barrier fails due to the formation...

The diffusion barrier property of 100-nm-thick titanium nitride (TiN) film between Cu and Si was investigated using sheet resistance measurements, etch-pit observation, x-ray diffractometry, Auger electron spectroscopy, and transmission electron microscopy. The TiN barrier fails due to the formation of crystalline defects (dislocations) and precipitates (presumably Cu-silicides) in the Si substrate which result from the predominant in-diffusion of Cu through the TiN layer. In contrast with the case of Al, it is identified that the TiN barrier fails only the in-diffusion of Cu because there is no indication of Si pits in the Si substrate. In addition, it appears that the stuffing of TiN does not improve the diffusion barrier property in the Cu/TiN/Si structure. This indicates that in the case of Al, the chemical effect that impedes the diffusion of Al by the reaction of Al with $TiO_{2}$ which is present in the grain boundaries of TIN is very improtant. On the while, in the case of Cu, there is no chemical effect because Cu oxides, such as $Cu_{2}O$ or CuO, is thermodynamically unstable in comparison with $TiO_{2}$. For this reason, it is considered that the effect of stuffing of TiN on the diffusion barrier property is not significant in the Cu/ TiN/Si structure.