초록

용어보기논문에서 용어와 풀이말을 자동 추출한 결과로, 시범 서비스 중입니다. AI-Helper

Abstract ▼ AI-Helper

The amount of Cr(Ⅲ) and Cr(Ⅵ) in a chromium plating solution could be determined simultaneously within five minutes using UV/VIS spectrophotometer coupled with a flow-through analysis(FTA) setup. The λmax's at 580 nm and 440 nm which correspond to Cr(Ⅲ) and Cr(Ⅵ), respectively, well obey the Beer-La...

The amount of Cr(Ⅲ) and Cr(Ⅵ) in a chromium plating solution could be determined simultaneously within five minutes using UV/VIS spectrophotometer coupled with a flow-through analysis(FTA) setup. The λmax's at 580 nm and 440 nm which correspond to Cr(Ⅲ) and Cr(Ⅵ), respectively, well obey the Beer-Lambert law in the range over 0.05 g/L for Cr(Ⅲ) and 0.005 g/L for Cr(Ⅵ). when the pH of the sample is less than 4.0, the absorption extinction coefficients of those peaks are not much dependent on the proton concentration. The amount of Cr(Ⅲ) and Cr(Ⅵ), and the total chromium in post treatment chromium plating solution, which normally has few g/L of Cr concentration, could be easily measured using UV/VIS spectrophotometry after the sample had been diluted with sulfuric acid of pH=1.0 in the flow-through analysis setup; this method is far more convenient and faster than the common redox titration (which requires at least 40 min/sample) method, while the accuracy of the method is highly comparable to conventional titrimetric method. Since the implementation of an PTA-UV/VIS setup in any plating industry is cost effective and easy to operate, the analytic method described in this paper may be applied directly for in situ analysis of plating solutions.