Crystallization characteristics of titanium oxide thin film during post-annealing of reactive sputter deposition were studied. Amorphous phases of as-deposited films were crystallized into rutile after annealing at $900^{\circ}C$ and anatase at $500^{\circ}C$, respectively when...

Crystallization characteristics of titanium oxide thin film during post-annealing of reactive sputter deposition were studied. Amorphous phases of as-deposited films were crystallized into rutile after annealing at $900^{\circ}C$ and anatase at $500^{\circ}C$, respectively when $O_2$ concentration during sputtering was more than 15%. However, rutile was the only phase obtainable after annealing if %$O_2$ was less than 10%. For these films, Magneli phase($Ti_nO_{2n-1}$) were crystallized below $500^{\circ}C$ at first place due to slow oxidation of nonstoichiometric films but $500^{\circ}{\sim}600^{\circ}C$ anatase with nonstoichiometry was crystallized for a short period. It was, therefore, concluded that crystal growth can proceed without phase transition if stoichiometric phase is formed at the first stage of crystallization, and that rutile, the most stable phase, was resulted from any oxygen deficient nonstoichiometric films.