To enhance the strength and formability of MCFC matrixes, alumina/${\gamma}$-LiAlO2 fiber-reinforced ${\gamma}$-LiAlO2 ma-trixes have been investigated. The MCFC matrixes with the thickness of 500~600 ${\mu}{\textrm}{m}$ were prepared by tape-casting of the slurry c...

To enhance the strength and formability of MCFC matrixes, alumina/${\gamma}$-LiAlO2 fiber-reinforced ${\gamma}$-LiAlO2 ma-trixes have been investigated. The MCFC matrixes with the thickness of 500~600 ${\mu}{\textrm}{m}$ were prepared by tape-casting of the slurry containing 10~30wt% fibers, followed by heat-treating up to $650^{\circ}C$. The porosity of fi-ber-reinforced matrixes decreased with the content of fibers, while the appropriate porosity(50~60%) for MCFC matrixes could be attained by adding larger ${\gamma}$-LiAlO2 particles with the diameter of about 50${\mu}{\textrm}{m}$ up to 50 wt%. The optimum length and content of the alumina fiber, both in the alignment of fibers and the enhancement of the strength, were found to be below 250${\mu}{\textrm}{m}$ and 20 wt%, respectively. On the other hand, the strength(156 gf/$\textrm{mm}^2$) of the ${\gamma}$-LiAlO2 matrix reinforced with ${\gamma}$-LiAlO2 fibers prepared in this study was improved by 20~40% in comparison with the alumina-fiber-reinforced matrix. It was also found that the alu-mina-fiber-reinforced matrix was completely corroded in molten carbonates but the ${\gamma}$-LiAlO2 was not.

주제어