In order to make high purity materials including low contents of interstitial impurities, 70 ㎾ electron beam melter was manufactured. The sponge Ti and Ti-6Al-4V alloy were required and melted by electron beam melter. Based on the experimental results of sponge Ti refining by electron beam melting, ...

In order to make high purity materials including low contents of interstitial impurities, 70 ㎾ electron beam melter was manufactured. The sponge Ti and Ti-6Al-4V alloy were required and melted by electron beam melter. Based on the experimental results of sponge Ti refining by electron beam melting, the purity of Ti was increased for 180 seconds but thereafter did not significantly vary. In addition, it was found that with number of melting, the purity of Ti did and vary but the yield of Ti was decreased. As a results of Ti refining, high purity Ti of 3N (99.9 wt%) could be obtained including interstitial impurities with total contents of which were maximum 900 ppm. From the experimental results of Ti-6Al-4V alloy electron beam melting, the amounts of Al loss could be estimated through thermodynamic data calculated from the regular solution model and the model of solute removal kinetics and the alloy composition calculated from the models was in accord with the experimental composition of the alloy, It took 10 minutes to make Ti-29Al-4V alloy calculated from the model into Ti-6Al-4V alloy and the composition of Ti-6Al-4V alloy was very homogeneous.