Polyisobutenylsuccinic anhydride(PIBSA), an intermediate for the lubricating oil additive, was prepared by the reaction of polyisobutylene(PIB) with maleic anhydride (MA). The functionality, which indicates the extent of reaction of PIB-a and MA, was determined in the various reaction conditions : f...

Polyisobutenylsuccinic anhydride(PIBSA), an intermediate for the lubricating oil additive, was prepared by the reaction of polyisobutylene(PIB) with maleic anhydride (MA). The functionality, which indicates the extent of reaction of PIB-a and MA, was determined in the various reaction conditions : fuctionality was 0.98 under the reaction conditions of no solvent for 12 hours at $190^{\circ}C$, 0.21 in benzyl alcohol solvent for 12 hours at $190^{\circ}C$, and 0.03~0.20 with various Lewis acids such as $AlCl_3$, $SnCl_4$, $Et_2AlCl$, and $TiCl_4$. The fuctionality also depended on the structure of PIBs. As ${\alpha}$-olefin content (exo-form) in PIB increased, the fuctionality had a higher value. The structure of PIBSA prepared from PIB and MA was determined with FT IR and $^1H$ NMR spectroscopy. Two strong anhydride IR bands at 1782 and $1855cm^{-1}$ were obserbed and two IR bands at 1639 and $897cm^{-1}$ for unsaturated groups of PIB disappeared. The presence of the anhydride was difficult to find by $^1H$ NMR spectroscopy because the anhydride protons gave relatively small peaks over a 2.0~3.0 range. Polyisobutenylsccinimide (PIBSI), a lublicating oil additive, was prepared by the reaction of PIBSA with diaminoethane.