In relation to the application of magnetic method to the evaluation of irradiation damage (embrittlement) changes in the magnetic parameters(hysteresis loop and Barkhausen noise) and Vickers microhardness due to neutron irradiation and heat treatment were measured and compared. In the case of irradi...

In relation to the application of magnetic method to the evaluation of irradiation damage (embrittlement) changes in the magnetic parameters(hysteresis loop and Barkhausen noise) and Vickers microhardness due to neutron irradiation and heat treatment were measured and compared. In the case of irradiation $(2.3{\times}10^{19}\;n/cm^2,\; E{\ge}1\;Mev,\; 288{\circ}C)$ hysteresis loop measurements show that susceptibility decreases as coercivity increase. Saturation magnetization do not show any change. Barkhausen noise amplitude and Barkhausen noise energy have decreased while Vickers microhardness has increased. For isothermally heat treated condition of irradiated specimen at 470 $^{\circ}C$ and 540 $^{\circ}C$, Barkhausen noise energy has increased while Vickers microhardness has decreased. Results of BNE and Vickers microhardness are reversed to the results on irradiated condition. All these consistent changes in magnetic parameter and Vickers microhardness measurement, which are thought to be resulted from the interaction between irradiation-induced defects and dislocation, and magnetic domain, respectively, show a possibility that magnetic measurement may be used to the evaluation of material degradation and recovery due to neutron irradiation and heat treatment, respectively, if a relevant large database in prepared.