초록

용어보기논문에서 용어와 풀이말을 자동 추출한 결과로, 시범 서비스 중입니다. AI-Helper

Abstract ▼ AI-Helper

Standard Zircaloy-4 sheets, charged with 230-250ppm hydrogen by the gas-charging method and homogenized at $400^{\circ}C$ for 72hrs in a vacuum, were corroded in pure water and aqueous LiOH solutions using static autoclaves at $350^{\circ}C$. Their corrosion behaviors were char...

Standard Zircaloy-4 sheets, charged with 230-250ppm hydrogen by the gas-charging method and homogenized at $400^{\circ}C$ for 72hrs in a vacuum, were corroded in pure water and aqueous LiOH solutions using static autoclaves at $350^{\circ}C$. Their corrosion behaviors were characterized by measuring their weight gains with the corrosion time and observing their microstructures using an optical microscope and a scanning electron microscope. The elemental depth profiles for hydrogen and lithium were measured using a secondary ion mass spectrometry(S1MS) to confirm their distributions at the oxidelmetal interface. The normal Zircaloy-4 specimens corroded abruptly and heavily at the concentration of Li ions more than 30ppm in the aqueous solution. This is due to accelerations by the rapid oxidation of many Zr- hydrides formed by the large amount of absorbed hydrogen, resulting from the increased substitution of $Li^{+}$ ions with $Zr^{4+}$-sites in the oxide as the Li ion concentration increased. The specimens that had been charged with amounts of hydrogen greater than its solubility corroded early with a more rapid acceleration than normal specimens, regardless of the corrosion solutions. At longer corrosion times. however, normal specimens showed a rather accelerated corrosion rate compared to the hydrogen-charged specimens. These slower corrosion rates of the hydrogen-charged specimens at the longer corrosion times would be due to the pre-existent Zr-hydride in the matrix, which causes the hydrogen pick- up into the specimen to be depressed, when the oxide with an appropriate thickness formed.