Poly(phenylene sulfide-co-phenylene sulfide sulfone), PPS/PPSS copolymers were synthesized from p-dichlobenzene(DCB), p-dibromobenzene(DBB), p-diiodobenzene(DIB), 4-chlorophenyl sulfone(CPS) and sodium sulfide as comonomers under high temperature and pressure utilizing N-methyl-2-pyrrolidinone(NMP) ...

Poly(phenylene sulfide-co-phenylene sulfide sulfone), PPS/PPSS copolymers were synthesized from p-dichlobenzene(DCB), p-dibromobenzene(DBB), p-diiodobenzene(DIB), 4-chlorophenyl sulfone(CPS) and sodium sulfide as comonomers under high temperature and pressure utilizing N-methyl-2-pyrrolidinone(NMP) as solvent. The yield of PPS/PPSS copolymer shoed maximum at $190^{\circ}C$ with [DBB]/[CPS] and [DIB]/[CPS] comonomer pair, while [DCB]/[CPS] pair exhibited maximum yield at $230^{\circ}C$. The change of yield is in the order of I>Br>Cl as leaving groups were in accordance with nucleophilic aromatic substitution reaction mechanism suggested for the synthesis of PPS type polymers. The molecular weight of PPS/PPSS copolymer was the highest($M_w=8,330g/mol$) with [DBB]/[CPS] comonomers in which [CPS] was 10 mole%. The PPS/PPSS copolymer made with 10 mole% of [CPS] showed about $15^{\circ}C$ higher $T_g$ and $15^{\circ}C$ lower $T_m$ than those of PPS homopolymer, which may be useful from the processing and thermal property point of view. The PPS/PPSS copolymer with 30 mole% of CPS or above did not exhibit Tm. The PPS/PPSS copolymer obtained with comonomer feed ratio of [DBB]/[CPS] = 95/5 mole% under $240^{\circ}C$ showed even higher molecular weight($M_w=10,300g/mole$) than PPS homopolymer made under similar reaction condition, retaining high crystallinity and thermal stability.