To accelerate the curing and to improve the bonding properties of urea-melamine-formaldehyde (UMF) resin adhesives for plywood, the effects of resin compositions and additives on gelation time and bonding strength were discussed. The gelation time of UMF resin prepared by simultaneous reaction with ...

To accelerate the curing and to improve the bonding properties of urea-melamine-formaldehyde (UMF) resin adhesives for plywood, the effects of resin compositions and additives on gelation time and bonding strength were discussed. The gelation time of UMF resin prepared by simultaneous reaction with urea(U), melamine(M) and formaldehyde(F) at M/U molar ratio 0.2 was shortened as the molar ratio of formaldehyde to urea was increased. However, at F/U molar ratios higher than 2.5, the amounts of free fomaldehyde of resin could not satisfy with KS standard, Therefore, it was difficult to increase the amount of formaldehyde in resin composition for the purpose of fast gelation time. With increasing the molar ratio of melamine to urea(M/U) from 0.3 to 0.6 at constant F/U molar ratio 3.4, the gelation time of UMF resin was slightly decreased, while gradually increased at M/U molar ratio higher than 0.6. The gelation properties of UMF resin and bonding strength of UMF-bonded plywood could be enhanced by using ammonium chloride and p-toluene sulfonic acid as a curing-agent together with wheat flour and corngluten powder as a extender.

주제어