초록

용어보기논문에서 용어와 풀이말을 자동 추출한 결과로, 시범 서비스 중입니다. AI-Helper

Abstract ▼ AI-Helper

Three-point bending fatigue properties of austenitic 304 stainless steel sheets were investigated at room temperature and LNG temperature($-162^{\circ}C$) in the strain range from 0.43 to $1.7\%$. The fatigue properties at $-162^{\circ}C$ were superior to those at ro...

Three-point bending fatigue properties of austenitic 304 stainless steel sheets were investigated at room temperature and LNG temperature($-162^{\circ}C$) in the strain range from 0.43 to $1.7\%$. The fatigue properties at $-162^{\circ}C$ were superior to those at room temperature due to the higher volume fractions of deformation-induced martensite. The cyclic hardening behavior owing to the deformation- induced martensite transformation was detected in both specimens. In room temperature testing, the mean load amplitude increased steadily with cycles, meaning that cumulative plastic incubation strain was required for martensite transformation. On the contrary, in $-162^{\circ}C$ tested specimen, the mean load amplitude increased rapidly within a few cycles due to the rapid transformation of martensite, and slightly decreased after the maximum is reached probably due to dynamic recovery.

주제어