Mullite was synthesized by adding industrial by-products, Al(OH)3 and boehmite, to a natural kaolin of pink A-grade. The attrition milling method, which has simultaneously milling and mixing effects, was carried out. The specimens were formed by uni-axial pressing of 1.5 ton/$\textrm{cm}^2$

Mullite was synthesized by adding industrial by-products, Al(OH)3 and boehmite, to a natural kaolin of pink A-grade. The attrition milling method, which has simultaneously milling and mixing effects, was carried out. The specimens were formed by uni-axial pressing of 1.5 ton/$\textrm{cm}^2$ and then fired. When the Al(OH)3 was added, the flexural strength of 71.8 wt% Al2O3 specimen fired at 1600$^{\circ}C$ for 4 hrs was 22.3 MPa and the amount of synthesized of 71.8 wt% Al2O3 specimen fired at 1600$^{\circ}C$ for 10 hrs was about 85%. When the boehmite was added, the flexural strength of 68 wt% Al2O3 speciment fired at 1600$^{\circ}C$ for 10 hrs was 147 MPa, and the high purity mullite of about 95% was synthesized for 71.8 wt% Al2O3 specimen fired at 1600$^{\circ}C$ for 10 hrs.

주제어