Si3N4 -Si3N4 joints were made using Ag-Cu-Ti and Ag-Cu-In-Ti via brazing method and the change in joint strength was investigated after heat treatment at $400^{\circ}C$ or $650^{\circ}C$ for up to 2000h. The initial strength of as-brazed joints with Ag-Cu-In-Ti was lower but th...

Si3N4 -Si3N4 joints were made using Ag-Cu-Ti and Ag-Cu-In-Ti via brazing method and the change in joint strength was investigated after heat treatment at $400^{\circ}C$ or $650^{\circ}C$ for up to 2000h. The initial strength of as-brazed joints with Ag-Cu-In-Ti was lower but the reduction of the strength was less dramatic than that with Ag-Cu-Ti. The joints made of a new brazing alloy Au-Ni-Cr-Mo-Fe which is developed for high temperature applications were heat-treated at $650^{\circ}C$ for 1000h. As the heat treatment time increased the bond strength increased. The results of the joining system with Mo or Cu interlayer showed that the strength of the joint with Mo interlayer was higher but the system incurred problems in joint production Also it was found from oxidation experiment that Ti and In affected the oxidation resistance of brazing alloy.

주제어