An FBAR(Solidly Mounted Resonator) was fabricated using reflector layers which prohibit the penetration of bulk acoustic wave into substrate. The SMR consisted of top and bottom electrodes(Al films), a piezoelectric layer (ZnO film), reflector layers(W/$Si_2$ films) and Si substrate. The ...

An FBAR(Solidly Mounted Resonator) was fabricated using reflector layers which prohibit the penetration of bulk acoustic wave into substrate. The SMR consisted of top and bottom electrodes(Al films), a piezoelectric layer (ZnO film), reflector layers(W/$Si_2$ films) and Si substrate. The electrodes were deposited by dc sputtering. The piezoelectric layer and the reflector layers were deposited by rf magnetron sputtering. The control of crystallinity, microstructures and electric properties of each layer was essential for attaining the optimum FBAR characteristics. Under the best deposition conditions for FBAR devices, the ZnO films had highly c-axis preferred orientation(${\sigma}=2.17^{\circ}$), resistivity of $10^4\;{\omega}cm$, and surface roughness of 10.6 ${\AA}$. On the other hand, the surface roughness of W and $Si_2$ films was 16 ${\AA}$ and 33 ${\AA}$, respectively, and the resistivity of Al film was $5.1{\times}10^{-6}\;{\Omega}cm$. The SMR devices were fabricated by the conventional semiconductor processes. In the resonance conditions of the SMR, the series resonance frequency (fs) and the parallel resonance frequency(fp) were 1.244 GHz and 1.251 GHz, respectively and the quality factor(Q) was 1200.