When a zinc-oxide eugenol type sealer was placed in root canals treated previously with calcium hydroxide, acceleration of its setting and the yellowish discoloration were observed clinically. The purpose of this study was to evaluate the properties of calcium hydroxide-eugenol compound. Some physic...

When a zinc-oxide eugenol type sealer was placed in root canals treated previously with calcium hydroxide, acceleration of its setting and the yellowish discoloration were observed clinically. The purpose of this study was to evaluate the properties of calcium hydroxide-eugenol compound. Some physical properties of calcium hydroxide-eugenol compound were compared with a manufactured zinc-oxide eugenol based root canal sealer, Tubli-seal$^{(R)}$ in terms of water solubility, water sorption, film thickness and microleakage. Solubility and water sorption were determined by the use of the method described in American Dental Association Specification(ADAS) no. 57. Ten samples of each material were prepared into disks 20mm in diameter and 1.5mm in thickness. The samples were immersed in 50ml of distilled water at $37{\pm}1^{\circ}C$ for 7 days. The samples were then removed and placed in a desiccator. The values for solubility and water sorption were calculated using differences between the weights of same sample. Film thickness was determined by the use of the method described in ADAS no. 57 too. A small quantity of mixed cement was placed between two glass plates of which thickness was measured previously. 15Kg loading was applied and total thickness of the glass plates and the cement film was measured. The thickness difference was recorded as the material's film thickness. Microleakage was determined with a dye penetration method. Experimental materials were placed between the dentin surface of bovine tooth and the acrylic rod. These units were immersed in Pelican ink (W-Germany) for three days. Dye-penetrated dentin surfaces of bovine tooth were measured using the NIB Image 1.60 Macintosh program. The results are as follows: 1. Water solubility value of calcium hydroxide-eugenol compound (20.98${\pm}$2.94%) was statistically higher than those of Tubli-seal$^{(R)}$(2.52${\pm}$0.49%)(p<0.05). 2. Water sorption value of calcium hydroxide-eugenol compound (59.72${\pm}$17.75%) was statistically higher than those of Tubli-seal$^{(R)}$(3.15${\pm}$0.76%)(p<0.05). 3. Film thickness value of calcium hydroxide-eugenol compound (0.36${\pm}$0.03mm) was statistically higher than those of Tubli-seal$^{(R)}$(0.12${\pm}$0.1mm)(p<0.05). 4. Dye penetration value after 3 days-immersion of calcium hydroxide-eugenol compound(57.63${\pm}$25.85%) was statistically higher than those of Tubli-seal$^{(R)}$(28.05${\pm}$23.46%)(p<0.05).

주제어