Ceramic foam prepared with cordierite as a starting material by foam method was tested to evaluate the feasibility as a filter for the dust collection in hot gas. Two different types of agents Benzethonium chloride (BZTC, C27H42NO2Cl) and Sodium Lauryl Sulfate(SLS, CH3(CH2)11OSO3Na) were used as foa...

Ceramic foam prepared with cordierite as a starting material by foam method was tested to evaluate the feasibility as a filter for the dust collection in hot gas. Two different types of agents Benzethonium chloride (BZTC, C27H42NO2Cl) and Sodium Lauryl Sulfate(SLS, CH3(CH2)11OSO3Na) were used as foaming agents in foaming process. Porosityof ceramic foam was about 80% and mean pore size were 100${\mu}{\textrm}{m}$ for SLS agent and 200 ${\mu}{\textrm}{m}$ for BZTC. It was observed that ceramic foam was composed of continuous macro-pore structure with opening windows interconnecting macro-pores. The surface of ceramic foam support of was coated with cordierite particles ranged from 20${\mu}{\textrm}{m}$ to 50${\mu}{\textrm}{m}$ Meso-pore size in the coating layer on ceramic foam was below 10${\mu}{\textrm}{m}$. While air permeability of the support increased with increasing macro-pore size coated ceramic filters showed a constant permeability without regard to the macro-pore size of the support. The permeabuilities of support varied in the range of 600$\times$10-13m2 to 1000$\times$10-13m2. For the case of coated ceramic filter it was about 200$\times$10-13m2. As a result of particle trapping test by using fly ash the particle removal efficiency was over the 99.9%.

주제어