Sintering behaviors of the glass-alumina composites for low firing temperature were investigated as a function of the particle size of glass frit. The system of glass frit was Pb-B-Si-Al-O. The median particle sizes of the glass frits were 2.72$\mu\textrm{m}$, 2.67$\mu\textrm{m}$

Sintering behaviors of the glass-alumina composites for low firing temperature were investigated as a function of the particle size of glass frit. The system of glass frit was Pb-B-Si-Al-O. The median particle sizes of the glass frits were 2.72$\mu\textrm{m}$, 2.67$\mu\textrm{m}$ and 1.33$\mu\textrm{m}$, which were prepared with changing ball-milling times as 24 h, 48 h and 96 h. The glass-alumina composites showed maximum density at certain temperature, and further heating led to dedensification behaviors, so called over-firing. The sintering temperature, which showed maximum density, raised from 425$^{\circ}C$ to 475$^{\circ}C$ with increase of particle size of glass frit from 1.33$\mu\textrm{m}$ to 2.72$\mu\textrm{m}$. Especially, the over firing behaviors, which were occurred at high sintering temperatures, were greatly increased with decrease of particle size of glass frit.

Keyword