The flow melting behavior of the electrolytic tinplate during reflow treatment was investigated in terms of morphology and structure of coating layers which were electrodeposited with variation of electrolyte temperature. It was commonly found that the nucleation density of the electrodeposits showe...

The flow melting behavior of the electrolytic tinplate during reflow treatment was investigated in terms of morphology and structure of coating layers which were electrodeposited with variation of electrolyte temperature. It was commonly found that the nucleation density of the electrodeposits showed little difference with the electrolyte temperature, and the growth of electrodeposited tin occurred along direction of (002) plane. At low electrolyte temperature, the (002) plane of tin nucleated paralleling to the substrate and grew perpendicularly to the substrate, which rendered porous rod-like deposits. With increasing the temperature, the (002) plane nucleated declining $15^{\circ}$ to the substrate and also grew to the normal direction, which enabled lateral growth of the tin crystals and rendered compact deposits. During reflow treatment, the matte deposit transformed to the reflowed state via transition regions consisted of contraction, island formation, and wetting . The matte deposits formed at low temperature exhibited wide transition regions because of poor thermal transfer between crystals due to their porous nature. While that formed at high temperature transformed very rapidly to the reflowed state by enhanced thermal transfer between the compact crystals.