Sn-3.5Ag-xBi alloys with five different levels of Bi (0, 2.5, 4.8, 7.5, 10 wt%) were prepared for evaluating creep properties. Cast alloys were roiled and heat treated to provide stable microstructures during the subsequent creep tests, which were conducted under constant load using dog-bone specime...

Sn-3.5Ag-xBi alloys with five different levels of Bi (0, 2.5, 4.8, 7.5, 10 wt%) were prepared for evaluating creep properties. Cast alloys were roiled and heat treated to provide stable microstructures during the subsequent creep tests, which were conducted under constant load using dog-bone specimens. For the Bi containing alloys, creep strength showed the maximum around 2.5 wt%Bi and tended to decrease with increasing Bi content. The stress exponent of the alloy was around 4, suggesting typical dislocation creep, but the exponent was 2 for the 10 wt%Bi alloy, suggesting creep assisted by grain boundary Sliding. For the Bi containing alloys, the brittle fracture mode appeared showing small amount of reduction of area, while the ductile fracture mode was true for the Bi free alloy. Microstructural examination of ruptured specimens showed cavitations on grain boundaries normal to the load axis, and a significant of grain boundary sliding for the Bi containing alloys.

Keyword