In order to improve the microstructure of the strip cast Nd-Fe-B alloys that are frequently used for production of high energy sintered magnets, influence of various strip casting conditions on the microstructure and phase formation and distribution were investigated. Nd-Fe-B strips consisting of mi...

In order to improve the microstructure of the strip cast Nd-Fe-B alloys that are frequently used for production of high energy sintered magnets, influence of various strip casting conditions on the microstructure and phase formation and distribution were investigated. Nd-Fe-B strips consisting of microstructures suitable for preparation of high energy sintered magnets could be obtained when the wheel speed was below 5 m/s. The compositional limit that can avoid the crystallization of free iron in the as-cast state was estimated to be Nd$\_$14/Fe$\_$79/B$\_$7/. Regardless of the compositional variation, preferred orientation of Nd$_2$Fe$\_$14/B normal to the strip surface was always occurred below 5 m/s, which would eventually enhance the grain alignment during pressing the powder under a magnetic field. While the coercivity of the strip cast alloys increased with the increase of the wheel speed, mainly due to the refinement of Nd$_2$Fe$\_$14/B grains, it decreased with the reduction of Nd content in the alloy composition as the formation of free iron increased.

주제어