Glass composed of $Li_2$O.MgO. $MgF_2$.$SiO_2$.$B_2O_3$ for the fabrication of green sheet was prepared by melting process, and glass ceramics was prepared by the process of nucleation and grystal growth for the glass of $Li_2$O.MgO. $MgF_2...

Glass composed of $Li_2$O.MgO. $MgF_2$.$SiO_2$.$B_2O_3$ for the fabrication of green sheet was prepared by melting process, and glass ceramics was prepared by the process of nucleation and grystal growth for the glass of $Li_2$O.MgO. $MgF_2$.$SiO_2$.$B_2O_3$ system with Lithium fluorhectorite and Lithium boron fluorphlogopite crystal phase. Powderization of the glass ceramics was carried out by water swelling. The average particle size at this point was 2.574 $\mu\textrm{m}$. Slurry was prepared for green sheet using high viscous sol fabricated by water swelling, which shows cleavage phenomenon in prepared glass ceramics. The optimum ratio of powder to water for the tape casting was 18:100, and its viscosity was 11,000~14,000 cps.