Photodegradation characteristics of polyolefin composites were studied. Thermogravimetric analysis results suggest that the polyolefin blends used in this study have different amounts of talc. The mechanical behaviors of polyolefin blends, which experienced UV-irradiation in accordance with SAE J196...

Photodegradation characteristics of polyolefin composites were studied. Thermogravimetric analysis results suggest that the polyolefin blends used in this study have different amounts of talc. The mechanical behaviors of polyolefin blends, which experienced UV-irradiation in accordance with SAE J1960, are investigated using tensile and Izod impact tests. These results show that as the UV-exposure time increases, a significant drop in the elongation at break and impact strength at a low temperature are observed. This may be explained by the decreases in elastic energy derived from the scission of polymer molecular chains and the low density of entanglement after UV- photodegradation. Scanning electron microscopy observations indicate that no crack and surface damage are observed, while the additional talc particles are exposed, on the UV-exposed surfaces. The exposure of talc particles may be responsible for the discoloration of UV-exposed polyolefin blend surface. Observation using Fourier transform infrared spectroscopy (FT-IR) confirms the presence of photodegradation on the surface of UV-exposed polyolefin blend.

Keyword